利用熔盐法在260℃的低温下制备出了单相Ba1-xKxBiO3(BKBO,0.315≤x≤0.6)样品.磁性测量结果表明,在x值整个范围内的BKBO样品都表现出超导电性,x=0.4时,超导转变温度达到最高值(Tc=30.6 K):粉末X射线衍射结果表明,所有样品中均含有少量的BaCO3杂相,它是由于反应过程中Ba(OH)2·8H2O和空气中的二氧化碳反应造成的;扫描电镜观察BKBO微观形貌为片状.为与熔盐法作比较,利用溶胶.凝胶法制备Ba0.6K0.4BiO3,发现此法难以制备出单相BKBO样品.利用热分析和退火处理来研究熔盐法制备Ba0.6K0.4BiO3的热稳定性,发现样品大约在400℃开始分解,表明Ba0.6K0.4BiO3在400℃以上是不稳定的.
Ba1-xKxBiO3 (BKBO) samples with 0.315≤x≤0.6 were synthesized at a relatively low temperature of 260℃ by molten salt method. The superconductivity was tested in the whole range of x value, the highest superconducting transition temperature Tc= 30.6 K at x=0.4. X-ray Diffraction patterns reveal that small amount of impurity phase of BaCO3 were detected in BKBO which is images. For comparison, sol-gel method was also used in synthesizing Ba0.6K0.4BiO3 sample, but no single phase of BKBO was obtained. For the sample of Ba0.6K0.4BiO3 prepared by molten salt method, the therrnostability was investigated by thermo-gravimetric analysis (TGA) and annealing treatment, and the sample was decomposed at 400℃. The result showed that Ba0.6K0.4BiO3 was thermally unstable above 400 ℃.
参考文献
| [1] | Mattheiss L F;Gyorgy E M;Johnson D W .[J].Physical Review B:Condensed Matter,1988,37(07):3745. |
| [2] | Cava R J;Batlogg B;Krajewski J J et al.[J].Nature,1988,332:814. |
| [3] | Shiryaey S V;Barilo S N;Ustinovich S N et al.[J].Journal of Crystal Growth,2000,211(1-4):471. |
| [4] | Klinkova L A;Uchida M;Matsui Y et al.[J].Physical Review B:Condensed Matter,2003,67(14):140 501. |
| [5] | Kim DC.;Baranov AN.;Kim JS.;Kang HR.;Kim BJ.;Kim YC.;Pshirkov JS. Antipov EV.;Park YW. .High pressure synthesis and superconductivity of Ba1-xKxBiO3 (0.35 < x < 1)[J].Physica, C. Superconductivity and its applications,2003(4):343-353. |
| [6] | Sato H;Tajima S;Takagi H et al.[J].Nature,1989,338:241. |
| [7] | Yamamoto H;Aoki K;Tsukada A;Naito M .Growth of Ba1-xKxBiO3 thin films by molecular beam epitaxy[J].Physica, C. Superconductivity and its applications,2004(Pt.2):192-195. |
| [8] | Mijatovic D.;Rijnders G.;Hilgenkamp H.;Blank DHA.;Rogalla H. .Growth studies of Ba1-x(K-x)BiO3-delta thin films by pulsed-laser deposition[J].Physica, C. Superconductivity and its applications,2002(Pt.2):596-599. |
| [9] | Utz B.;Wiest F.;Prusseit W.;Berberich P.;Kinder H. .Ba<SUB>1-x</SUB>K<SUB>x</SUB>BiO<SUB>3</SUB> epitaxy on various substrate materials[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1995(2):1351-1354. |
| [10] | Jones N L;Parise J B;Flippen R B et al.[J].Journal of Solid State Chemistry,1989,78:319. |
| [11] | Zhao L Z;Yin B;Zhang J B et al.[J].Physica C,1997,282-287(02):723. |
| [12] | S.F.Liu;W.T.Fu .Synthesis of superconducting Ba-1-xK_xBiO_3 by a modified molten salt process[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2001(7-8):1505-1512. |
| [13] | RrhspringerJL;Niznansky D .[J].Journal of Alloys and Compounds,1993,195:73. |
| [14] | Nagata, Y.;Mishiro, A. .The normal-state transport properties of Ba1-xKxBiO3 crystals with a wide range of potassium compositions (0 less than or equal x less than or equal 0.62) were studied. Although the host material BaBiO3 has a monoclinic structure, the system changes[J].The journal of physics and chemistry of solids,1999(12):1933-1942. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%