为加强对油气管线钢腐蚀失效机理的认识,采用动态慢应变速率拉伸试验(SSRT),研究了弱酸性环境中富锌涂层与阴极保护对16Mn和X80 2种不同强度级别管线钢应力腐蚀开裂(SCC)敏感性的影响,探讨了2种管线钢的SCC机理.结果表明:在5%NaCl+0.5%CH3 COOH 酸性溶液中,16Mn钢的SCC机理以阳极溶解为主,富锌涂层和阴极保护均能有效提高16Mn钢的SCC抗力,前者效果优于后者;X80钢的SCC机理以氢脆为主,富锌涂层和阴极极化均促进其SCC过程,但富锌涂层提高X80钢SCC敏感性的程度低于与涂层自腐蚀电位相近的阴极极化作用.
参考文献
| [1] | 祝馨.长输管道的腐蚀与防护[J].石油化工腐蚀与防护,2006(01):51-53. |
| [2] | 王朝晖,李旭光.管道阴极保护的探讨[J].管道技术与设备,2004(01):35-38. |
| [3] | 胡士信,窦宏强,刘桂志,张万军,荀津辉.利此亚西部管道阴极保护技术[J].油气储运,2005(11):28-32. |
| [4] | 王崇.无机富锌涂料在炼油厂储油罐上的应用[J].石油化工腐蚀与防护,1990(04):35-39. |
| [5] | 张微,何莉萍,唐绍裘,赖琛.富锌环氧涂层的防腐蚀研究[J].涂料工业,2002(12):4-6. |
| [6] | Krzywicki J W.Zinc coatings:steel's corrosion inhibitor,multffaceted finish serves dual purpose in shielding steel substrates from atmospheric exposure while offering cathodic protection[J].American Galvanizers Association,2006(10):28-36. |
| [7] | Marchebois H.;Touzain S.;Joiret S.;Bernard J.;Savall C. .Zinc-rich powder coatings corrosion in sea water: influence of conductive pigments [Review][J].Progress in Organic Coatings: An International Review Journal,2002(4):415-421. |
| [8] | Konsowa A H;El-Shazly A H .Rate of zinc consumption during sacrificial cathodic protection of pipelines carting saline water[J].Desalination,2002,153:223-226. |
| [9] | 刘道新;金石 .300M超高强度钢的应力腐蚀开裂[J].特殊钢,1997,18(06):20-23. |
| [10] | 乔利杰;王燕彬;褚武扬.应力腐蚀机理[M].北京:科学出版社,1993:108-109. |
| [11] | 刘道新,金石.300M超高强度钢应力腐蚀敏感性及断口的分维特征[J].腐蚀科学与防护技术,1994(01):77. |
| [12] | A. Zielinski;P. Domzalicki .Hydrogen degradation of high-strength low-alloyed steels[J].Journal of Materials Processing Technology,2003(1/2):230-235. |
| [13] | Zucchi F;Grassi V;Monticelli C .Hydrogen embrittlement of duplex stainless steel under cathodic protection in acidic artificial sea water in the presence of sulphide ions[J].Corrosion Science,2006,48:522-530. |
| [14] | 李会录,惠卫军,王燕斌,董瀚,翁宇庆,褚武扬.高强钢应力腐蚀门槛值随强度的变化规律[J].金属学报,2001(05):512-516. |
| [15] | 郭浩,李光福,蔡珣,周建江,黄春波,杨武.外加电位对X70管线钢在近中性pH溶液中的应力腐蚀破裂的影响[J].中国腐蚀与防护学报,2004(04):208-212. |
| [16] | 张涛,孙新岭,陈居术,龙军,林梅.氢在高强度管道钢应力腐蚀中的作用[J].管道技术与设备,2004(02):33-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%