以Yb2O3-Al2O3体系为烧结助剂,采用气压烧结法制备了氮化硅陶瓷.研究了烧结温度对气压烧结氮化硅陶瓷的致密度、失重率、物相、力学性能与显微结构的影响及材料的烧结机理.结果表明:随着烧结温度的升高,氮化硅的致密度、抗弯强度、断裂韧性和硬度均呈现先增加后降低的趋势,而失重率呈现一直升高的趋势;当烧结温度为1780℃、烧结气压为6 MPa时,所得氮化硅烧结体的体积密度(3.31 g·cm-3)、抗弯强度(967.2)、断裂韧性(8.9 MPa·m1/2)和硬度(17.1 GPa)达最大值,晶粒以长柱状的β相为主;烧结温度高于或等于1700℃时,材料中的α相可完全转化为β相,β-Si3 N4晶粒的平均长径比达12.31.
参考文献
| [1] | Wang CM.;Hoffmann MJ.;Cannon RM.;Ruhle M.;Pan WQ..GRAIN BOUNDARY FILMS IN RARE-EARTH-GLASS-BASED SILICON NITRIDE[J].Journal of the American Ceramic Society,19963(3):788-792. |
| [2] | Wu, Tian-Li;Marcon, Denis;Ronchi, Nicolo;Bakeroot, Benoit;You, Shuzhen;Stoffels, Steve;Van Hove, Marleen;Bisi, Davide;Meneghini, Matteo;Groeseneken, Guido;Decoutere, Stefaan.Analysis of slow de-trapping phenomena after a positive gate bias on AlGaN/GaN MIS-HEMTs with in-situ Si3N4/Al2O3 bilayer gate dielectrics[J].Solid-State Electronics,2015Jan.(Jan.):127-130. |
| [3] | Krstic, Z.;Krstic, V.D..Silicon nitride: The engineering material of the future[J].Journal of Materials Science,20122(2):535-552. |
| [4] | 臧建兵;王明智;王艳辉.ZrO2（Y2O3）增韧的氮化硅烧结体的性能及相关系[J].复合材料学报,2000(4):76. |
| [5] | 于方丽;白宇;杜军;于平平;王俭志;杨建锋.β-Si3N4晶种的制备、性能与机理研究[J].人工晶体学报,2011(6):1595-1601. |
| [6] | 岳昌盛;彭犇;郭敏;张梅.β-SiAlON晶须的诱导合成和生长机制研究[J].人工晶体学报,2011(5):1181-1187. |
| [7] | 鲁元;杨建锋;陆伟忠;高积强;陕绍云.碳热还原-常压烧结法制备多孔氮化硅陶瓷[J].硅酸盐学报,2009(8):1277-1281. |
| [8] | 陈宇红;韩非;江涌;韩凤兰;吴澜尔.AlN-Y2O3液相烧结碳化硅陶瓷[J].兵器材料科学与工程,2009(5):1-3. |
| [9] | 时振海.两步气压烧结Si3N4陶瓷[J].佛山陶瓷,2000(05):19-20. |
| [10] | 戴金辉;李建保;杨晓战.β-Si3N4晶种的制备和自增韧Si3N4陶瓷[J].稀有金属材料与工程,2004(4):375-379. |
| [11] | Hirokazu Yamamoto;Katunori Akiyama;Yuichiro Murakami.Densification behaviors and high-temperature characteristics of Si_3N_4 sintered bodies using Al_2O_3-Yb_2O_3 additives[J].Journal of the European Ceramic Society,20066(6):1059-1067. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%