采用慢应变速率法和恒应变原位电化学测试法研究了水质稳定剂Rp-04L对304不锈钢在高硬循环冷却水中应力腐蚀行为的影响.结果表明:水质稳定剂Rp-04L对304不锈钢在高硬度循环冷却水中的应力腐蚀破裂有明显的抑制作用.当在冷却水中加入100 mg/L的Rp-04L时,304不锈钢的应力腐蚀敏感性明显降低.
参考文献
| [1] | Osama M. Alyousif;Rokuro Nishimura .The stress corrosion cracking behavior of austenitic stainless steels in boiling magnesium chloride solutions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(7):3040-3051. |
| [2] | Yamamoto K.;Hosoya K. .CORROSIVITY OF BR- AND CL- ON DUPLEX STAINLESS STEEL[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(1/2):239-243. |
| [3] | Rokuro Nishimura;Yasuaki Maeda .Stress corrosion cracking of type 304 austenitic stainless steel in sulphuric acid solution including sodium chloride and chromate[J].Corrosion Science,2004(2):343-360. |
| [4] | Toshio Shibata .Passivity breakdown and stress corrosion cracking of stainless steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(1):20-30. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%