采用正硅酸乙酯溶液和硅酸钙溶液对剑麻纤维进行改性,然后将其与聚丙烯树脂制成复合材料.研究了纤维处理后增重情况以及处理前后单纤维及复合材料的拉伸性能,利用红外光谱对处理前后的单纤维进行了表征与分析.结果表明,正硅酸乙酯溶液和硅酸钙溶液处理后单纤维及复合材料的拉伸性能得以提高,单纤维拉伸强度分别提高14.68%和13.15%,单纤维拉伸模量分别提高16.28%和11.22%.经正硅酸乙酯溶液和KH550硅烷溶液组合处理后,复合材料拉伸性能提高更加明显,拉伸强度和模量分别提高24.05%和58.33%.
参考文献
| [1] | Xue Li;Lope G. Tabil;Satyanarayan Panigrahi .Chemical Treatments of Natural Fiber for Use in Natural Fiber-Reinforced Composites: A Review[J].Journal of polymers and the environment,2007(1):25-33. |
| [2] | 徐峰,史铁钧,张克宏,王鹏.SiO2/杉木粉复合材料的制备和表征[J].复合材料学报,2007(03):84-88. |
| [3] | 符韵林,赵广杰,全寿京.二氧化硅/木材复合材料的微观结构与物理性能[J].复合材料学报,2006(04):52-59. |
| [4] | DIPA RAY;B K SARKAR;A K RANA .Effect of alkali treated jute fibres on composite properties[J].Bulletin of Materials Science,2001(2):129-135. |
| [5] | D.Bikiaris;P.Matzinos;A.Larena;V.Flaris;C.Panayiotou .Use of Silane Agents and Poly(propylene-g-maleic anhydride) Copolymer as Adhesion Promoters in Glass Fiber/Polypropylene Composites[J].Journal of Applied Polymer Science,2001(3):701-709. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%