The rates of growth of short fatigue cracks initiated from a notch are much greater than the rates of growth of long fatigue cracks for the same values of Delta K. A decrease in the strength of materials caused by aging affects the behavior of long cracks. The geometric form of the notch strongly affects the behavior of short cracks. The growth rate of a short crack initiated from a sharp notch decreases and attains a minimum value at a length of 0.45 mm, which is far beyond the region of its influence. However, short cracks initiated from blunt notches exhibit slower growth in the region of stress concentration than outside this region. Strain fields induced by deformation of the tip of the notch are not the only factor inhibiting the propagation of short cracks from notches. To explain the behavior of a short crack initiated at a notch, one must take into account some other factors, in particular, crack closure.

参考文献

上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%