以天然玄武岩为原料同时采用烧结和球磨两种工艺方法制备热喷涂粉体.球磨方法制备的喷涂粉体粒度为45～145 μm,烧结方法制备的粉体粒度小于80 μm.采用大气等离子热喷涂(APS)技术在45钢上喷涂玄武岩粉体.两种玄武岩粉体涂层与45钢基体均有良好的结合.用X射线衍射和SEM方法对非金属涂层结构进行分析.试验结果说明烧结玄武岩喷涂涂层后主要组织为非晶态结构,含有少量的晶体矿物和化合物,如尖晶石、磁铁矿、刚玉等.直接球磨玄武岩粉体喷涂形成的涂层组织结构主要以非晶态为主,含有少量晶体矿物如镁铁矿、磁铁矿和尖晶石等.
参考文献
| [1] | Yan Q Y;Tan H P;Shang D K .Physical properties of basalt and numerical simulation of the melting process in basalt particle beds[J].International Journal of Theoretical Physics,2001,22(03):995-1015. |
| [2] | HUSEYIN GUNERHAN;ARIF HEPBASLI .Utilization of Basalt Stone as a Sensible Heat Storage Material[J].Energy sources,2005(14):1357-1366. |
| [3] | 刘艳春,王芬,李建军.略阳玄武岩制造连续纤维的研究[J].硅酸盐通报,2008(01):160-164. |
| [4] | 李建军,刘艳春,陈继生.绿色玄武岩纤维成型的数值模拟方法[J].硅酸盐通报,2008(05):1076-1080. |
| [5] | P. Rohan;K. Neufuss;J. Matejficek .Thermal and mechanical properties of cordierite, mullite and steatite produced by plasma spraying[J].Ceramics International,2004(4):597-603. |
| [6] | Mostaghimi J.;Pasandideh-Fard M.;Chandra S. .Dynamics of splat formation in plasma spray coating process[J].Plasma Chemistry and Plasma Processing,2002(1):59-84. |
| [7] | Marple B R;Lima R S;Moreau C et al.Yttria-stabilized zirconia thermal barriers sprayed using N2-H2 and Ar-H2 plasmas:influence of processing and heat treatment on coating properties[J].Journal of Thermal Spray Technology,2007,16(5-6):791-797. |
| [8] | 谢先德,陈鸣,王德强,王英.动态高压下斜长石的熔融和玻璃化研究[J].岩石学报,2006(02):503-509. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%