采用循环极化、U型样法、慢应变速率拉升、金相表征等手段对比研究热处理制度对7150铝合金电化学腐蚀性能和应力腐蚀性能的影响;并从TEM晶界析出相分布、晶界腐蚀形貌、点蚀发生发展机理以及应力腐蚀开裂机制等角度,对电化学参数与应力腐蚀敏感性之间的一致性关系进行理论说明.结果表明:第二点蚀电位((Ψ)pit,2)及其相应电位差值((Ψ)pit,2-(Ψ)corr、(Ψ)pit,2-rep)随时效的变化趋势与耐应力腐蚀能力随时效的变化趋势完全一致.

参考文献

[1] Tolga Dursun;Costas Soutis.Recent developments in advanced aircraft aluminium alloys[J].Materials & design,2014Apr.(Apr.):862-871.
[2] 孙擎擎;孙睿吉;陈送义;陈启元;陈康华.大气污染物对7B50铝合金电化学腐蚀性能的影响[J].中国有色金属学报,2015(3):575-581.
[3] 张新明;李鹏辉;刘胜胆;李国锋;朱航飞;周新伟.回归时间对7050铝合金晶间腐蚀性能的影响[J].中国有色金属学报,2008(10):1795-1801.
[4] A.F. Oliveira Jr.;M.C. de Barros;K.R. Cardoso;D.N. Travessa.The effect of RRA on the strength and SCC resistance on AA7050 and AA7150 aluminium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20041/2(1/2):321-326.
[5] 孙擎擎;陈康华;陈启元.热处理制度对含Yb航空铝合金电化学腐蚀行为的影响[J].中国有色金属学报,2016(3):479-485.
[6] J.F. Li;N. Birbilis;C.X. Li.Influence of retrogression temperature and time on the mechanical properties and exfoliation corrosion behavior of aluminium alloy AA7150[J].Materials Characterization,200911(11):1334-1341.
[7] 杜爱华;龙晋明;裴和中.高强铝合金应力腐蚀研究进展[J].中国腐蚀与防护学报,2008(4):251-256.
[8] Qingjiang Meng;G. S. Frankel.Effect of Cu Content on Corrosion Behavior of 7xxx Series Aluminum Alloys[J].Journal of the Electrochemical Society,20045(5):B271-B283.
[9] D. McNaughtan;M. Worsfold;M.J. Robinson.Corrosion product force measurements in the study of exfoliation and stress corrosion cracking in high strength aluminium alloys[J].Corrosion Science,200310(10):2377-2389.
[10] 孙擎擎;董朋轩;孙睿吉;陈启元;陈康华.时效制度对挤压Al-6.2Zn-2.3Mg-2.3Cu铝合金电化学腐蚀性能的影响[J].中国有色金属学报,2015(4):866-874.
[11] D. Cicolin;M. Trueba;S. P. Trasatti.Effect of chloride concentration, pH and dissolved oxygen, on the repassivation of 6082-T6 Al alloy[J].Electrochimica Acta,2014:27-35.
[12] 彭国胜 .变形和热处理对Al-Zn-Mg-Cu系超强铝合金组织和性能的影响[D].中南大学,2011.
[13] G. S. Peng;K. H. Chen;S. Y. Chen;H. C. Fang.Influence of dual-RRA temper on the exfoliation corrosion and electrochemical behavior of Al-Zn-Mg-Cu alloy[J].Materials and Corrosion,20134(4):284-289.
[14] 董朋轩 .Al-8.54Zn-2.41Mg-xCu超强铝合金多相组织调控及性能研究[D].中南大学,2013.
[15] Uros Trdan;Janez Grum.Evaluation of corrosion resistance of AA6082-T651 aluminium alloy after laser shock peening by means of cyclic polarisation and E1S methods[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012Jun.(Jun.):324-333.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%