三(二苯甲酰甲烷)苯氧基钛酸酯[(dbm)3Ti(Oph)]在MAO作用下,催化p-甲基苯乙烯间规聚合.讨论了催化剂浓度、铝钛比和聚合温度对反应的影响;在催化剂浓度为350 μmol/L、铝钛比为500时,聚合活性最大为7.5×105 g/molTi·h.聚合物有两个熔点183 ℃、203 ℃,分别对应晶型Ⅰ和晶型Ⅲ,玻璃化转变温度为108 ℃左右.同时考察了在此催化体系下p-甲基苯乙烯与苯乙烯间规共聚的情况,苯乙烯和p-甲基苯乙烯的竞聚率分别为0.287、1.806.
参考文献
| [1] | Ishihara N;Seimiya T;Kuramoto M .[J].Macromolecules,1986,19:2464. |
| [2] | Soga K;Nakatani H;Monoi T .[J].MACROMOLECULES,1990,23:953-957. |
| [3] | Schwecke C.;Kaminsky W. .Homo- and copolymerization of styrene and alkylstyrenes with the highly active catalyst system CpTiF3/MAO[J].Macromolecular rapid communications: Publishing the newsletters of the European Polymer Federation,2001(7):508-512. |
| [4] | Li CL.;Chan SH.;Ting C.;Jiang GJ. .Synthesis and characterization of functionalized syndiotactic polystyrene copolymers[J].Journal of Applied Polymer Science,2002(4):1038-1045. |
| [5] | 阎卫东,陈金晖,周鼐,洪瀚,胡友良.间规聚苯乙烯的技术进展[J].石油化工,1999(10):716-721. |
| [6] | 阎卫东,洪瀚,周鼐,宓霞,谢光华,胡友良.MgCl2负载（dbm）2Ti（OPh）2催化乙烯聚合[J].高分子学报,2000(03):358. |
| [7] | Xia M;XU D;YAN W .[J].高分子通报,2002,47:521. |
| [8] | Rosa C D;Esposito S;Buono A et al.[J].Polymer,2003,44:1655. |
| [9] | Tomotsu N.;Newman TH.;Malanga MT.;Ishihara N. .Syndiospecific polymerization of styrene[J].Journal of molecular catalysis, A. Chemical,1998(1/3):167-190. |
| [10] | Chien J C W;Salajka Z .[J].Journal of Polymer Science Part A:Polymer Chemistry,1991,29:1243. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%