一种消除粉末高温合金中PPB的方法

钢铁研究学报, 2003, 15(z1): 513-518.

1.钢铁研究总院高温材料研究所,北京,100081

2.钢铁研究总院高温材料研究所,北京,100081

3.钢铁研究总院高温材料研究所,北京,100081

4.钢铁研究总院高温材料研究所,北京,100081

Method of Elimination PPB in P/M Superalloy

采用等离子旋转电极工艺(PREP)制备的镍基高温合金粉末,经过1170℃热等静压(HIP)固结和热处理后,组织中存在原始颗粒边界(PPB).PPB上析出物主要由γ'相和少量NbC、TiC组成.采用高温固溶处理工艺,结果表明,经过1160℃,4h,空冷固溶处理,可以消除PPB,炉冷效果比空冷差.

[1]	Allen R E;Bartos J L;Aldred P .[P].US patent: 3890816,1975.
[2]	Dahlén M;Winberg L.[J].Metal Science Journal,1979(3-4):163-169.
[3]	Dahlén M;Ingesten N G;FischmeisterH.[J].Mod Dev Powder Metall,1981:3-14.
[4]	Dahlén M;Fischmeister H.[J].Superaloys,1980:449-454.
[5]	Davidson J H;Aubin C.[J].High Temperature Materials and Processes,1982:853-886.
[6]	Ingesten N G;Warren R;Winberg L .[Z].High Temperature Alloy for Gas Tubine,1982.
[7]	Warren R;Ingcsten N G;Winberg L et al.[J].PM,1984,27(03):141-146.
[8]	Marguez C;Esperance G;Koul A K .[J].International Journal of Powder Metallurgy,1989,25(04):301-308.
[9]	Maurer G E;Castledine W .[J].Superaloys,1996,1996:645-652.
[10]	Pierron X;Banik A;Maurer G E et al.[J].Superalloys,2000,2000:425-433.
[11]	Белоs АФ;АношкинНФ;ФаткyллинОНидр.ЖаропрочныеиЖаростойскиесталииславынаникелевойоcнове[M].М::наyка,1984:31-41.
[12]	EрёменкоВИ;АношкинНФ;ФаткyллинОН.[J].МиТОМ,1991(12):8-11.
[13]	李慧英;胡本芙;章守华等.[J].金属学报,1987,23B(02):90-94.

上一张下一张

计量

作者相关

文章评分