本文采用化学共沉淀法制备一系列配比的三元 Sn1-x-yMnxSbyO2(y=0.05)固溶体,利用 XRD、TG-DTA 等分析了在 600~1000℃退火温度下的固溶体物相组成,并根据分析结果绘制了该固溶体在固相线下的相图,进而探讨了 Sn1-x-yMnxSbyO2(y=0.05)固溶体的形成机制.结果表明:在600~1000℃退火温度下,Sn0.9Mn0.05 Sb0.05O2 固溶体只存在四方金红石相的SnO2物相,锑和锰主要以Sb5+、Mn3+、Mn4+的形式进入SnO2晶格形成有限固溶体;Sn0.7Mn0.25Sb0.05O2 和 Sn0.6Mn0.35Sb0.05O2 固溶体在 700℃、800℃出现了立方相方铁锰矿型 Mn2O3,1000℃出现了四方相黑锰矿型 Mn3O4,Sn0.6Mn0.35Sb0.05O2 固溶体在1000℃时还出现Sb3+Sb5+O4 物相;固相线下 Sn1-x-yMnxSbyO2(y=0.05)固溶体相图包括六个区域,其中富含锡的(Sn,Mn,Sb)O2ss 区域是唯一的单相区,锰和锑主要分别以 Mn2O3 和Sb2O5 的形式溶入 SnO2 晶格中,并达到饱和.(Sn,Mn,Sb)O2ss 固溶体氧化物可作为良好导电性和耐腐蚀性的阳极中间层材料.

参考文献

[1] Galliard-Allemand B;Podor R;Vilasi M et al.Experimental Study of the SnO2-ZrO2 Phase Diagram[J].Journal of the European Ceramic Society,2002,22:2297-2303.
[2] Xueming Chen;Guohua Chen .Stable Ti/RuO{sub}2-Sb{sub}2O{sub}5-SnO{sub}2 electrodes for O{sub}2 evolution[J].Electrochimica Acta,2005(20):4155-4159.
[3] T. El Moustafid;H. Cachet;B. Tribollet;D. Festy .Modified transparent SnO{sub}2 electrodes as efficient and stable cathodes for oxygen reduction[J].Electrochimica Acta,2002(8):1209-1215.
[4] Yu H C;Shen P Y .Phase Transformations and Micrestructures of TiO2-SnO2 Due to Solution Annealing Versus Reactive Sintering[J].Journal of the European Ceramic Society,2008,28(01):91-99.
[5] L.B. Kong;J. Ma;H. Huang .Preparation of the solid solution Sn_(0.5)Ti_(0.5)O_2 from an oxide mixture via a mechanochemical process[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):315-319.
[6] Bueno P R;Leite E R;Bulohes L O S et al.Sintering and Mass Transport Features of(Sn,Ti)O2 Polycrystalline Ceramics[J].European Ceramic Society,2003,23(06):887-896.
[7] Hu Y H;Zhang H H;Yang H M .Synthesis and Electrical Proporty of Antimony-Doped Tin Oxide Powders with Barite Matrix[J].Journal of Alloys and Compounds,2008,453(1-2):292-297.
[8] Baker PGL;Sanderson RD;Crouch AM .Sol-gel preparation and characterisation of mixed metal tin oxide thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2007(17):6691-6697.
[9] Pyke D R;Reid R;Tilley R J D et al.Structures of Tin Oxide-Antimony Oxide Catalysts[J].Journal of the Chemical Society,Faraday Transactions,1980,76:1174-1182.
[10] 徐加荣,朱克荣,戚梦瑶,庄永龙.氧化锡纳米晶的合成与生长[J].人工晶体学报,2010(04):912-916.
[11] Jun-Jie Zhu;Jian-Min Zhu;Xue-Hong Liao .Rapid synthesis of nanocrystalline SnO_2 powders by microwave heating method[J].Materials Letters,2002(1/2):12-19.
[12] Ebber D;Kieβing D;Schmitz W et al.MnOx/ZrO2 Catalysts for the Total Oxidation of Methane and Chloyomethane[J].Applied Catalysis B:Environmental,2004,52(02):135-143.
[13] 胡学兵,周健儿,徐小勇,汪永清,张小珍.In掺杂对化学共沉淀法合成的SnO_2粉体Zeta电位的影响[J].人工晶体学报,2009(06):1485-1488.
[14] Gao KH;Li ZQ;Liu XJ;Song W;Liu H;Jiang EY .Bulk Sn1-xMnxO2 magnetic semiconductors without room-temperature ferromagnetism[J].Solid State Communications,2006(4):175-178.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%