研究了玻璃纤维增强溴化环氧乙烯基酯树脂复合材料（ GFRC ）光老化前后力学性能及其变化规律；用SEM和XPS对GFRC的表面微观形貌及元素变化进行检测分析；FTIR和同步热分析用来研究树脂光老化过程中的分子结构的变化规律和高温分解情况。结果表明，加速光老化之后GFRC的力学性能变化不大，有较好的拉伸强度、弯曲强度和压缩强度保留率；加速光老化过程中GFRC表面的树脂发生较明显的变化，出现了颜色变深，树脂脱落等老化现象；由于玻璃纤维的存在阻止了GFRC内部树脂基体的进一步老化。
Mechinical properties of glass fiber/brominated epoxy vinyl ester composites ( GFRC) were studied af-ter the accelerated light agingtest.Surface Micromorphology and Elements changes of GFRC in the aging process were researched by scanning electron microscope ( SEM) and X-ray photoelectron spectroscopy ( XPS) ,respectively.The results showed that the GFRC keeped perfect mechinical properties ,such as perfect retention in tensil ,bend, and compressive strength ,after being exposed under the light a period of time.The color of the GFRC surface be-came darker and a small section of the ester falled off from the GFRC surface.Fourier transform infraed spectrsco-py( FTIR) and themo analysis showed that the continued aging of the internal ester was prevented by the surface glass fiber.
参考文献
| [1] | 陆士平,王天堂.溴化环氧乙烯基酯树脂的性能与应用[J].玻璃钢/复合材料,2002(02):35-37. |
| [2] | 常源亮;刘耀德.新型溴化环氧树脂类阻燃剂[J].山东化工,1998(02):41-47. |
| [3] | 钟方国.环氧乙烯基酯树脂种类及性能[J].纤维复合材料,2005(01):60-64. |
| [4] | 张锐,郑威,袁秀梅,高泉喜,王昭亮.复合材料的真空辅助成型工艺研究[J].工程塑料应用,2005(06):33-35. |
| [5] | 李华,冯圣玉,金子明.玻璃纤维增强乙烯基酯树脂抗冲击复合材料的研究[J].工程塑料应用,2006(04):17-20. |
| [6] | 张德庆.高分子材料导论[M].哈尔滨:哈尔滨工业大学出版社,1999:33-35. |
| [7] | 寒冬冰;王慧敏.高分子材料概论[M].北京:中国石化出版社,2003:51-53. |
| [8] | 谭晓倩,史鸣军.高分子材料的老化性能研究[J].山西建筑,2006(01):179-180. |
| [9] | 贾修伟 .高分子量溴化环氧树脂阻燃剂制备研究[D].河南大学,2003. |
| [10] | 龚兵,李玲,董凤云,孙丽转.阻燃性乙烯基酯树脂复合材料的研究[J].纤维复合材料,2006(04):14-17. |
| [11] | 吴舜娟,冯志新,尹文华.玻璃纤维增强复合材料的人工加速老化性能研究[J].合成材料老化与应用,2013(04):10-13. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%