利用微乳液法制备出纳米复合Ag-Fe合金,在真空条件下,利用高速摄影机观测Ag-Fe系列合金的阴极斑点运动,采用示波仪记录放电电流曲线,并利用扫描电子显微镜观察电极表面烧蚀状况.研究结果表明:Fe纳米粒子的加入使得电弧分散,电孤的寿命增加,截流值降低.
Nanosized Ag-Fe composite alloy was synthesized through reverse micelles microemulsion to measure the vacuum arc characteristics on this material. Vacuum arc cathode spots were observed by using high speed photography and oscillograph was used to record discharge current curve. The morphology of erosion on cath-ode after discharge was characterized by scanning electron microscopy (SEM). The result indicated that the arc spots was more dispersive, arc lifetime was more long, chopping current was smaller after iron nanoparticles was doped in silver contact material.
参考文献
| [1] | Beilis I L .[J].IEEE Transactions on Plasma Sciences,2001,29(05):657-670. |
| [2] | Yang Zhimao et al.[J].Vacuumm,2006,81:545-549. |
| [3] | Lafferty J M.Theory and Application[M].New York:wiley,1980 |
| [4] | 杨志懋 .合金元素、显微组织对真空触头材料耐电压强度,分断电流能力和截流值的影响[D].西安:西安交通大学,1996. |
| [5] | Gleiter H;Weissmuller J;Wollersheim O et al.[J].Acca Mater,2001,49:737-745. |
| [6] | Sosa E D .The electron Emission Characteristics of Aluminum,Molybdenum and Carbon Nanotubes Studied by Field Emission and Photoemission[D].USA:University of North Texas,2002. |
| [7] | Hentzsche E .[J].IEEE Transactions on Plasma Sciences,2003,31:799-808. |
| [8] | 王庆丰,崔树茂,张锐丽,杨生春,杨志懋,丁秉钧.纳米CuCr25合金的阴极斑点运动特性[J].稀有金属材料与工程,2008(04):641-643. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%