通过对00Cr17Ti经热带退火、不经热带退火两种工艺的冷轧板进行对比试验,在分析显微组织、织构的基础上,研究了热带退火对00Cr17Ti薄板表面皱折的影响.研究结果表明:与不经热带退火相比,经热带退火能使成品薄板的表面皱折大大减轻,最大粗糙度仅为12.06 μm,平均粗糙度仅为1.27μm.两种工艺的成品板表面皱折程度的不同是由两者在显微组织、微织构上的差异造成的.与不经热带退火相比,经热带退火的成品薄板在板厚方向具有较均匀的组织,板宽方向的织构梯度较小,晶粒簇较间断、细窄、分散,所有这些使得成品薄板的表面皱折大大减轻.为了满足用户对薄板表面质量的严格要求,对热轧带进行退火是很有必要的.
参考文献
| [1] | Tsuchiyama T;Hirota R;Fukunaga K et al.Ridging-Free Ferfitic Stainless Steel Produced Through Recrystallization of Lath Martensite[J].ISIJ International,2005,45(06):923. |
| [2] | Hyung-Joon Shin;Joong-Kyu An;Soo Ho Park;Dong Nyung Lee .The effect of texture on ridging of ferritic stainless steel[J].Acta materialia,2003(16):4693-4706. |
| [3] | SooHo PARK;Kwang Yuk KIM;YongDeuk LEE .Evolution of Microstructure and Texture Associated with Ridging in Ferritic Stainless Steels[J].ISIJ International,2002(1):100-105. |
| [4] | Hamada J I;Matsumoto Y;Fudanoki F et al.Effect of Initim Solidified Structure on Ridging Phenomenon and Texture in Type 430 Ferritic Stainless Steel Sheets[J].ISU International,2003,43(12):1989. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%