采用浆料包渗法,以B4C为供硼剂,NH4Cl+KBF4为复合活化剂,SiC为填充剂,蛋白质(鸡蛋清)为粘结剂,在W6Mo5Cr4V2高速钢表面制备渗硼层.研究了渗硼温度对渗硼层组织和性能的影响.结果表明:包渗温度650℃时,渗硼层组织以Fe2B相为主,在750℃、850℃时,形成了V2B3相,在950℃时渗硼层组织中出现了Fe2Si04B06相;渗硼层的显微硬度随温度的升高先增后降低,其最小显微硬度值为810 HV,为基体的(235 HV) 3.5倍;渗硼层最小摩擦系数为0.12,为基体的1/3.磨损机制在750℃时发生转变,由粘着磨损为主转变为磨料磨损为主.

参考文献

[1] WANG Hongfu,WANG Huachang,WANG Xiao.Ni60-SiC Coating Prepared by Plasma Spraying, Plasma Re-melting and Plasma Spray Welding on Surface of Hot Forging Die[J].武汉理工大学学报(材料科学版)(英文版),2011(04):715-718.
[2] X.X. Mei;W.F. Sun;S.Z. Hao;T.C. Ma;C. Dong .Surface modification of high-speed steel by intense pulsed ion beam irradiation[J].Surface & Coatings Technology,2007(9/11):5072-5076.
[3] MEI Xian-xiu,HAO Sheng-zhi,MA Teng-cai,WANG Ying-min,LIU Zhen-min.The Effect of Intensity Pulsed Ion Beam Irradiation on Wear Resistance of High-speed Steel[J].材料热处理学报,2004(05):1049-1052.
[4] H. Huang;X. Wang;J. He .Synthesis and properties of graphite-like carbon by ion beam-assisted deposition[J].Materials Letters,2003(22/23):3431-3436.
[5] 项东,许斌,刘科高.W6Mo5Cr4V2激光熔覆陶瓷涂层显微组织及性能分析[J].激光技术,2003(05):434-436.
[6] 张光胜,赵翔,章宗城,许忠胜.W6Mo5Cr4V2钢氮离子注入表面改性层的摩擦学性能[J].摩擦学学报,2001(06):410-415.
[7] Li CM;Shen BL;Li GJ;Yang C .Effect of boronizing temperature and time on microstructure and abrasion wear resistance of Cr12Mn2V2 high chromium cast iron[J].Surface & Coatings Technology,2008(24):5882-5886.
[8] Li C;Li MS;Zhou YC .Improving the surface hardness and wear resistance of Ti3SiC2 by boronizing treatment[J].Surface & Coatings Technology,2007(12):6005-6011.
[9] M.A. Bejar;R. Henriquez .Surface Hardening Of Steel By Plasma-electrolysis Boronizing[J].Materials & design,2009(5):1726-1728.
[10] Mu, Dong;Shen, Bao-luo;Yang, Chao;Zhao, Xin .Microstructure analysis of boronized pure nickel using boronizing powders with SiC as diluent[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2009(12):1481-1484.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%