研究了轧制方式、轧制温度等对喷射共沉积7075/SiCp复合材料挤压板材成形性能、显微组织和力学性能的影响.结果表明:挤压变形可以提高7075/SiCp喷射共沉积坯的轧制变形性能,平行于挤压方向取样并进行交叉轧制可以制备出高质量、高性能的薄板;轧制变形对挤压过程中形成的SiC颗粒条带状不均匀分布有显著的改善作用,随着轧制变形量的增加,SiC颗粒分布趋于均匀;轧制过程中,SiC颗粒破碎,尺寸明显变小,形貌呈钝化趋势;7075/SiCp复合材料薄板(T6态)的力学性能为:σs＝536.2MPa,σb＝670.2MPa,δ＝4.8%.
参考文献
| [1] | 崔岩.碳化硅颗粒增强铝基复合材料的航空航天应用[J].材料工程,2002(06):3-6. |
| [2] | Miller W S;Zhuang L;Bottenm J et al.Recent development in aluminum alloy for the automotive industry[J].Materials Science and Engineering A,2000,280:37-49. |
| [3] | RAKAND H J;Hiskanen P W.Deformation structures and flow stress in aluniminum containing short whisker[J].Light Metal Age,1984:223-226. |
| [4] | Ibrahim I A;Mohamed F A;Lavernia E J et al.Particulate reinforced metal matrix composites-a review[J].Journal of Materials Science,1991,26:1137-1155. |
| [5] | 胡明,费维栋,姚忠凯,王德尊.非连续增强金属基复合材料的变形行为[J].宇航材料工艺,2001(01):10-14. |
| [6] | 胡代忠,陈礼清,赵明久,毕敬,徐永波.SiC颗粒增强铝基复合材料薄板的力学性能[J].中国有色金属学报,2000(06):827. |
| [7] | 赵明久,肖伯律,刘越,毕敬.碳化硅颗粒增强铝基复合材料（SiCp/2024Al）的热变形行为[J].中国有色金属学报,2002(z1):137-141. |
| [8] | 陈礼清;吕毓雄;毕敬 .SiCp增强铝基复合板材力学性能与晶粒取向分布[J].金属学报,1998,34(11):1183-1187. |
| [9] | 郭成,程羽,尚春阳,苏文斌,许建群.SiC颗粒增强铝合金基复合材料断裂与强化机理[J].复合材料学报,2001(04):54-57. |
| [10] | 陈振华,陈鼎,康智涛,严红革,张福全,袁武华,王慧敏.坩埚移动式喷射共沉积制取铝基复合材料的技术[J].湖南大学学报(自然科学版),2002(06):22-30. |
| [11] | 詹美燕,匡勇,周明,夏伟军.多孔金属及合金成形过程中的致密化与变形理论研究[J].稀有金属与硬质合金,2002(04):42-47. |
| [12] | 王祝堂;田荣璋.铝及铝合金加工手册[M].长沙:中南工业大学出版社,2000:68-79,454-457. |
| [13] | Manoharan M;Lewandowski J J .Effect of reinforcement size and matrix microstructure on the fracture properties of an Al metal matrix composite[J].Materials Science and Engineering A,1992,150:179-186. |
| [14] | Lee K B;Kwon H .Strength of Al-Zn-Mg-Cu Matrix composite reinforced with SiCp[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2002,33:455-465. |
| [15] | Semiatin S L;Seetharaman V .Deformation and microstructure development during hot- pack rolling of a near gamma titanium aluminum alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1995,26:371-381. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%