对GCr15在精炼过程产生的夹杂物进行分析，为减少夹杂、提升钢材质量奠定理论基础。采用金相、电子探针、光谱等方法，取样分析了西宁特钢EAF-LF-VD-CC流程冶炼的CA2r15在LFVD精炼时非金属夹杂物数量和尺寸的变化，并确定了各工位的夹杂类型和形成原因。试验结果表明，精炼过程夹杂总量一直呈下降趋势。LF精炼后，各尺寸夹杂数量明显变少，主要为尺寸较大的钙铝酸盐和含铝镁钙的复合夹杂；VD脱气后，粒径大于20tzm的夹杂完全上浮去除，残余夹杂主要为粒径小于10μm的钙铝酸盐和硅铝酸盐。根据分析结果，应优化冶炼工艺，增大对小尺寸夹杂物的去除率，同时应控制Ti、N的含量，避免TiN夹杂在钢液凝固过程中的析出和聚集。
It can provide theoretical basis for inclusion reduction and quality promotion through investigating the be havior of GCrl5 inclusions in refining process. Changes in value and size for non-metallic inclusions of GCrl5 in LF-VD refining were analyzed and the types and formation reason of inclusions in all stages were discussed for the process of EAF-LF-VD-CC in Xining Special Steel by the methods of metallo-graphy, electron probe and spectrographic analysis. The results show that the number of inclusions is less and less in the refining process. After the LF refining, all inclusions become less apparently and are mainly CaO-Al2O3 and CaO-Al2O3-MgO that have bigger sizes. At the end of VD, the inclusions which are greater than 20μm have been eliminated completely; the remaining inclusions are mainly CaO-Al2O3 and SiO2-Al2O3 that are less than 10μm. According to the analysis result, the smelting process should be optimized in order to increase the removal ratio of small size inclusions. At the same time,titanium and nitrogen content should be controlled to avoid the precipitation and agglomeration of TiN inclusions during solidification process.
参考文献
| [1] | 钟挹秀 .轴承钢材质与轴承寿命的关系[J].钢铁,1981,16(06):42. |
| [2] | 王进,孙维.硅钡合金在炼钢脱氧中的应用研究[J].炼钢,2000(04):37-41. |
| [3] | 贾品贵,倪华,李聿军,张家泉.底吹氩钢包冶金的流动和混合特性分析[C].第十二届全国炼钢学术会议,2002:272-278. |
| [4] | 于平 .高品质轴承钢工艺控制研究[D].北京:北京科技大学,2004. |
| [5] | 吴惠荣.钡合金处理对轴承钢脱氧及钢中夹杂物的研究[J].江苏冶金,2007(05):11-15. |
| [6] | 唐海燕,李京社,王剑斌,孙开明,温德松.钢包炉精炼不同吹氩工艺对夹杂物去除效果的研究[J].钢铁,2007(04):21-23,29. |
| [7] | 傅杰 .合金钢中的氮、钛控制[J].中国稀土学报,2000,18(09):394. |
| [8] | 田新忠;刘润藻 .轴承钢中TiN夹杂物的控制研究[J].北京科技大学学报,2009,30(03):152. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%