以四乙基溴化铵为模板剂,用原位水热合成法在α-Al2O3陶瓷管上合成出丝光沸石膜,系统研究了合成母液的组成、晶化时间、老化时间、硅源和铝源以及氟化钠助剂的添加等因素对丝光沸石膜成膜和表面形貌的影响. 结果表明,老化可使成膜沸石的晶粒从30 μm减小到5 μm; 添加氟化钠也能减小晶粒的大小; 使用异丙醇铝为铝源能制得高度定向的丝光沸石膜. 提出了丝光沸石膜的成膜机理,认为成核发生在载体表面,凝胶层的晶化过程是从载体的表面开始,不断转化,充分生长后达到凝胶层的表面. 丝光沸石膜对醇/水混合体系的分离研究表明,水/甲醇、水/乙醇、水/正丙醇和水/异丙醇的分离因子分别可达到1!500(323 K,水含量xw=15%),4!200(343 K,xw=15%),4!200(343 K,xw=50%)和3!400(343 K,xw=50%),所合成的丝光沸石膜能选择性地透过水,对醇/水混合物有较高的分离系数.
参考文献
| [1] | Bein T .[J].Chemistry of Materials,1996,8(08):1636. |
| [2] | 张延风,卢冠忠,许中强,陈庆龄.MFI型分子筛膜的制备与表征[J].催化学报,2000(05):447-450. |
| [3] | 徐晓春;程谟杰;杨维慎;林励吾 .[J].中国科学B辑,1998,28(03):247. |
| [4] | Dong J;Lin Y S .[J].Industrial and Engineering Chemistry Research,1998,37(06):2404. |
| [5] | Kondo M.;Kita H.;Okamoto K.;Komori M. .TUBULAR-TYPE PERVAPORATION MODULE WITH ZEOLITE NAA MEMBRANE[J].Journal of Membrane Science,1997(1):133-141. |
| [6] | Kumakiri I;Yamaguchi T;Nakao S .[J].Industrial and Engineering Chemistry Research,1999,38(12):4682. |
| [7] | Okamoto K;Kita H;Horii K;Tanaka K .[J].Industrial and Engineering Chemistry Research,2001,40(01):163. |
| [8] | Lin X;Kikuchi E;Matsukata M.[J].Chemical Communications,2000(11):957. |
| [9] | Shaikh A A;Joshi P N;Jacob N E;Shiralkar V P .[J].Zeolites,1993,13(07):511. |
| [10] | Matsufuji T;Nishiyama N;Ueyama K;Matsukata M .[J].Microporous and Mesoporous Materials,1999,32(1-2):159. |
| [11] | Piera E.;Coronas J.;Menendez M.;Santamaria J.;Salomon MA. .Synthesis, characterization and separation properties of a composite mordenite/ZSM-5/chabazite hydrophilic membrane[J].Journal of Membrane Science,1998(1):99-114. |
| [12] | 张延风,许中强,陈庆龄.小晶粒丝光沸石膜的制备与表征[J].催化学报,2002(02):145-149. |
| [13] | Sun Y;Song T;Qiu S .[J].Zeolites,1995,15(08):745. |
| [14] | Nakazawa T;Sadakata M;Okubo T .[J].Microporous and Mesoporous Materials,1998(21):325. |
| [15] | Lai R;Yan Y;Gavalas G R .[J].Microporous and Mesoporous Materials,2000,37(1-2):9. |
| [16] | Jansen J C;van Rosmalen G M .[J].Journal of Crystal Growth,1993(128):1150. |
| [17] | Jansen J C;Nugroho W;van Bekkum H;von Ballmoos R Higgins J B.[A].Boston Butterworth-Heinemann,1993:247. |
| [18] | Koegler J H;Zandbergen H W;Harteveld J L N;Nieuwenhuizen M S Jansen J C van Bekkum H .[J].Studies in Surface Science and Catalysis,1994(84):307. |
| [19] | Koegler J H;van Bekkum H;Jansen J C .[J].Zeolites,1997,19(04):262. |
| [20] | den Exter M J;van Bekkum H;Rijn C J M;Kapteijn F Moulijn J A Schellevis H Beenakker C I N .[J].Zeolites,1997,19(01):13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%