采用动电位极化曲线和电化学阻抗谱(EIS)研究了常温下国产904L不锈钢在不同浓度食品级磷酸中的腐蚀行为,并观察电化学测试后的腐蚀形貌.结果表明,国产904L不锈钢在25％食品级磷酸中具有良好的耐腐蚀性能,随着磷酸浓度的增加,自腐蚀电流密度Jcorr先增加后降低,浓度在40％时Jcorr最大,抗腐蚀性能最差.EIS曲线由高频端容抗弧和低频端Warburg阻抗组成,表明904L的腐蚀由电化学反应控制转为主要由扩散控制.
参考文献
| [1] | 江镇海.904 L钢的耐腐蚀特点及在磷复肥中的应用[J].腐蚀与防护,2009(11):764,767. |
| [2] | 吴洪特,于兵川.湿法磷酸中不锈钢腐蚀的电化学分析[J].全面腐蚀控制,2003(03):8-12. |
| [3] | S.Ahmad;A.U.Malik .Corrosion behaviour of some stainless steels in chlorinated Gulf seawater[J].Journal of Applied Electrochemistry,2001(9):1009-1016. |
| [4] | A. Alamr;D. F. Bahr;Michael Jacroux .Effects of alloy and solution chemistry on the fracture of passive films on austenitic stainless steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(4):925-936. |
| [5] | H. Hocheng;P.S. Kao;Y.F. Chen .Electropolishing of 316L Stainless Steel for Anticorrosion Passivation[J].Journal of Materials Engineering and Performance,2001(4):414-418. |
| [6] | Stephen P. Gaydos .Passivation of Aerospace Stainless Parts With Citric Acid Solutions[J].Plating & Surface Finishing,2003(3):20-25. |
| [7] | 程学群,李晓刚,杜翠薇,杨丽霞.316L不锈钢在醋酸溶液中的钝化膜电化学性质[J].北京科技大学学报,2007(09):911-915. |
| [8] | 安百刚,张学元,韩恩厚,李洪锡.Zn在模拟酸雨溶液中及其液膜下的腐蚀[J].金属学报,2004(02):202-206. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%