分别采用固相反应-放电等离子体烧结法(SR-SPS)和球磨-放电等离子体烧结法(MG-SPS)两种方法,系统研究了制备工艺对NixCo4-xSb12(x=0.1～0.5)化合物结构和热电性能的影响规律.研究表明:两种制备工艺对于化合物的物相结构及赛贝克系数的影响差异不大,但在Ni含量较低的情况下,SR-SPS的制备工艺增大了材料的电阻率和晶粒尺寸,使材料热导率增加,从而导致热电性能的降低;与SR-SPS相比,MG-SPS方法不但简便快捷,降低能耗,更有利于材料热电性能的提高;本实验范围内,采用MG-SPS方法制备的Ni0.2Co3.8Sb12烧结体在温度T=773 K时,其无量纲热电性能指数ZT达到了0.6.
参考文献
| [1] | Jeitschk W;Braun D .[J].Acta Crystal,1997,B33:3401. |
| [2] | Stadnyk Yu;Gorelenko Yu;Tkachuk A et al.[J].Journal of Alloys and Compounds,2001,32:37. |
| [3] | Kitagawa H.;Hasaka M. .Skutterudite structure and thermoelectric properties in spin-cast Fe_xCo_yNi_zSb_(24) (x+y+z=8) ribbons[J].Scripta materialia,2000(8):727-731. |
| [4] | Anno H;Akai K;Nagao J.20th International Conference on Thermoelectrics[C].Piscataway:Institute of Electrical and Electronic Engineers,2001:101. |
| [5] | Nolas GS.;Slack GA.;Cohn JL. .Effect of partial void filling on the lattice thermal conductivity of skudderudites[J].Physical Review.B.Condensed Matter,1998(1):164-170. |
| [6] | Chen L D;Tang X F;Goto T et al.[J].Materials Research,2000,15:276. |
| [7] | 唐新峰;陈立东;Goto T et al.[J].中国科学B辑,2000,43:306. |
| [8] | 张久兴,刘科高,周美玲.放电等离子烧结技术的发展和应用[J].粉末冶金技术,2002(03):129-134. |
| [9] | 张久兴,刘科高,王金淑,周美玲,左铁镛.放电等离子烧结钼的组织和性能[J].中国有色金属学报,2001(05):796-800. |
| [10] | Nygren M;Shen Zhijian.NEDO International Symposium on Functionally Graded Materials[C].Mielparque,Tokyo:NEDO,1999:115. |
| [11] | Masao Tokita.NEDO International Symposium on Functionallly Graded Materials[C].Mielparque,Tokyo:NEDO,1999:23. |
| [12] | 刘科高,张久兴,路清梅,张隆,周美玲.CoSb3纳米晶块体热电材料的制备研究[J].稀有金属材料与工程,2004(03):329-332. |
| [13] | 张久兴,张隆,路清梅,刘科高,刘丹敏,周美玲,左铁镛.N型La0.9NixCo4-xSb12化合物的制备及热电性能研究[J].功能材料与器件学报,2004(01):59-62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%