Luminescent Properties of BaMgAl10O17: Eu2+ Phosphors Coated with Y2SiO5

稀土学报(英文版), 2006, 24(2): 143-145.

^1, , ^2, , ^3, , ^4, , ^5,

1.National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals, Grirem Advanced Materials Co. Ltd., Beijing 100088, China

2.National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals, Grirem Advanced Materials Co. Ltd., Beijing 100088, China

3.National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals, Grirem Advanced Materials Co. Ltd., Beijing 100088, China

4.National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals, Grirem Advanced Materials Co. Ltd., Beijing 100088, China

5.National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals, Grirem Advanced Materials Co. Ltd., Beijing 100088, China

基金项目: MOST of China(2006CB601104) 中国科学院资助项目(50272013;50204002)

Luminescent Properties of BaMgAl10O17: Eu2+ Phosphors Coated with Y2SiO5

Keywords： BAM

BaMgAl10O17: Eu2+ phosphors was prepared by the solid-reaction method.Y2SiO5 was coated uniformly on the surface of phosphor by the surface-coated method, and the luminescent and deterioration properties were discussed.The XRD and SEM results show that Y2SiO5 film is produced on the surface of BAM phosphor.The emission spectrum analysis shows that the peak of the phosphor does not change after coating.The two phosphors were applied to lamps and the deterioration was tested at different ignited time.The keep ratio of luminous flux of the phosphor coated with Y2SiO5 is higher than that of the uncoated phosphor.

参考文献

[1]	Oshio S;Matsuoka T;Tanaka S et al.Mechanism of luminance decrease in BaMgAl10O17:Eu2+ phosphor by oxidation[J].Journal of the Electrochemical Society,1998,145:3903.
[2]	Oshio S;Kitamula K;Shigeta T et al.Firing technique for preparing a BaMgAl10O17:Eu2+ with controlled particle shape and size[J].Journal of the Electrochemical Society,1999,146:392.
[3]	Koile J.Present and future and prospects of phosphors for plasma display[A].,1997:617.
[4]	Ushirozawa M.Luminance degradation of blue phosphor BaMgAl10O17:Eu2+ for PDP[A].:224.
[5]	邓朝勇,庄卫东,何大伟,王永生,康凯,黄小卫.Preparation and Luminescent Properties of BAM Blue Phosphor for PDP and CCFL[J].稀土学报(英文版),2004(01):108-113.
[6]	彭国贤.PDP用荧光粉的亮度衰减[J].电子器件,2001(03):245-251.
[7]	Tang Mingdao.The surface and interface problem of lamp luminescent materials[J].Chinese Journal of Luminescence,1992(01):1.
[8]	Chau C N;Silloway T V;Salvi P W .Phosphor powder for coating lamp envelopes and method for preparation[P].EP 0852255A2,1997.
[9]	Fan C W;Benjamin D E;Kummer F et al.Boron oxide coated phosphor and method of making same[P].US 5985175,1999.
[10]	Bethtel H;Czarnojan W;Mayr W et al.Aluminate phosphor with a polyphosphate coating[P].US 5998047,1999.
[11]	Yang Hua;Wang Xiaojun;Duan Guihua et al.Luminescent properties of BaMgAl10O17:Eu2+ phosphors modified with MgF2[J].Materials Letters,2004,58:2374.
[12]	Hua Yang;Jingzhe Zhao;Lizhu Song .Photoluminescent properties of ZnS:Mn nanocrystals prepared in inhomogeneous system[J].Materials Letters,2003(15):2287-2291.
[13]	Yang H;Wang Z;Song L et al.Study of optical properties of manganese doped ZnS nanocrystals[J].Materials Chemistry and Physics,1997,47:249.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Luminescent Properties of BaMgAl10O17: Eu2+ Phosphors Coated with Y2SiO5

参考文献