采用显微激光喇曼光谱及XRD测量、表征了C/C复合材料中炭纤维、沥青炭及CVD热解炭经不同温度石墨化处理后的结构参数.结果表明:在3种炭材料的喇曼图谱上都有2个散射强度峰-D峰和G峰,峰位分别位于喇曼位移约1333及1584cm-1处,随石墨化处理温度改变,2峰峰位没有变化,但2峰相对强度却发生变化.将D峰相对于G峰的强度R的倒数R-1与XRD法得到的石墨化度g比照,发现2者存在一一对应关系,符合公式:g=1-exp[-2.11(R-1-0.34)].

The structural parameters of carbon fiber, pitch-derived carbon and pyrolytic carbon in C/C composites were charaterized by laser Raman microspectroscopy and
XRD. In Raman spectra of these carbons, two bands named D and G were observed near 1336.73cm-1 and 1581.00cm-1 respectively, the peak positions do
not but the relative intensities of the two bands change with heat treatment temperatures. The relationship between the XRD data of graphitization degree g
and R-1 where R is the relative intensity of band D to band G was plotted, the result shows that g increases with the increase of R-1, but the gradient
of the R-1-g curve decreases and gradually tends to zero with the increase of R-1, and their relation can be written into the following equation:
g=1-e-2.11(1/R-0.34). The foundation of the correlation between R-1 and g makes it possible to analyze the local distribution of graphitization degree in C/C composites.

参考文献

[1] 钱崇梁, 周桂芝, 黄启忠. 中南工业大学学报, 2001, 32(3): 285--288.
[2] Aladekomo J B, Bragg R H. Carbon, 1990, 28(6): 897--906.
[3] Nemanich R J, Solin S A. Phys. Rev., 1979, B20(2): 392--401.
[4] Tuinstra F, Koenig J L. The Journal of Chemical Physics, 1970, 53(3): 1126--1130.
[5] Leszek Nikiel, Paul W Jagodzinski. Carbon, 1993, 31(8): 1313--1317.
[6] Nakamizo M, Kammereck R, Walker P L, et al. Carbon, 1974, 12: 259--267.
[7] 张福勤, 黄伯云, 黄启忠, 等. 矿冶工程, 2000, 20(4): 10--13.
[8] Lieberman M L, Pierson H O. Carbon, 1974, 12: 233--241.
[9] Barry Granoff. Carbon, 1974, 12: 405--416.
[10] Kastner J, Pichler T, Kuzmany H. Chemical physics letters, 1994, 221(1/2): 53--58.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%