采用丝网印刷法制备了氧化钨纳米线敏感膜,系统研究了不同热处理温度下敏感膜的结构、形貌以及对CO气体的气敏性能.结果表明,氧化钨纳米线敏感膜具有较高的结构稳定性,经450℃热处理后其结晶取向和结构均未发生变化;热处理温度的升高有助于提高敏感膜的晶化程度,同时导致其表面的氧化钨纳米棒逐渐变短、变粗直至消失,并最终形成较大的纳米颗粒;经300℃热处理的敏感膜在300℃时对1×10 叫CO气体具有最佳的气敏性能,其灵敏度为17.64,响应时间为8s,恢复时间为16s.
参考文献
| [1] | Pinna N;Neri G;Antonietti M et al.[J].Angewandte Chemie International Edition,2004,43:4345-4349. |
| [2] | Khatko V;Calderer J;Llobet E et al.[J].Sensors and Ac-tuators B,2005,109:128-134. |
| [3] | Jimenez I;Centeno MA;Scotti R;Morazzoni F;Arbiol J;Cornet A;Morante JR .NH3 interaction with chromium-doped WO3 nanocrystalline powders for gas sensing applications[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2004(15):2412-2420. |
| [4] | Ivanov P;Llobet E;Blanco F;Vergara A;Vilanova X;Gracia I;Cane C;Correig X .On the effects of the materials and the noble metal additives to NO2 detection[J].Sensors and Actuators, B. Chemical,2006(1/2):311-317. |
| [5] | Zakrzewska K .Gas sensing mechanism of TiO2-based thin films[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2004(2):335-338. |
| [6] | Azad AM;Hammoud M .Fine-tuning of ceramic-based chemical sensors via novel microstructural modification - I: Low level CO sensing by tungsten oxide, WO3[J].Sensors and Actuators, B. Chemical,2006(2):384-391. |
| [7] | Ruiz A;Sakai G;Cornet A et al.[J].Sensors and Actua-tots B,2003,93:509-518. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%