利用溶剂法制备了热浸镀铝试样,借助扫描电镜观察了其微观形态,其镀层扩散层主要由Fe2Al5相构成.分析了750℃时不同浸镀时间下热浸镀扩散层的厚度,利用菲克第二定律对热浸镀扩散层的生长规律进行了理论分析,结合实验数据分析得知在浸镀时间延长时,镀层中Fe2 Al5相会有横向生长,使得扩散层厚度与时间的平方根呈现速率下降的抛物线规律.
参考文献
| [1] | 华勤;戚飞鹏 .钢铁零件热浸镀铝技术的发展[J].机械工程材料,1995,19(01):32. |
| [2] | Wei-Jen Cheng;Chaur-Jeng Wang .Observation of high-temperature phase transformation in the Si-modified aluminide coating on mild steel using EBSD[J].Materials Characterization,2010(4):467-473. |
| [3] | Bouche K.;Coulet A.;Barbier F. .Intermetallic compound layer growth between solid iron and molten aluminium[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):167-175. |
| [4] | Gul Hameed Awan;Faiz ul Hasan .The morphology of coating/substrate interface in hot-dip-aluminized steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):157-165. |
| [5] | 夏原 .钢材浸铝和浸扩铝工艺及表层组织性能的研究[D].哈尔滨工业大学,1995. |
| [6] | GB/T 18592-2001.GB/T 18592-2001,金属覆盖层钢铁制品热浸镀铝技术条件[S].北京:中国标准出版社,2004. |
| [7] | 铁铝原子在金属间化合物形成的扩散[J].上海大学学报(自然科学版),1998(06):661. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%