通过二次冷轧铜棒并850℃恒温热处理,制备出具有较强立方织构的Cu基带。以硝酸银、亚硫酸钠和硫代硫酸钠为主要原料配制镀银液,在立方织构Cu基带上制备出具有较强Ag（200）择优取向的银镀层。在600℃恒温热处理30min后Ag膜仍具有（200）择优取向,而830℃热处理后,Ag会扩散到Cu基底中,重复镀银、热处理5次后,Ag膜具有（200）的择优取向并少量面内织构,所得Ag/立方织构Cu复合带材可作为第二代高温超导带材YBCO涂层导体的金属基底。
Cubic textured Cu tapes were prepared by cold rolling twice combined 850℃ post heat treatment.Uniform Ag films were deposited on cubic textured Cu tapes by electroless plating with silver nitrate,sodium sulfite and sodium thiosulfate as the main raw materials.Ag films retained（200） preferred orientation when heated to 600℃ holding for 30min.But when the temperature was raised to 830℃,Ag films spreaded to Cu substrates.Only after repeated electroless plating silver and 830℃ heat treatment five times,Ag films showed（200） preferred orientation and a small amount of in-plane texture.The final Ag/cubic textured Cu composite tapes can be metallic substrates of the second generation high temperature tapes YBCO coated conductor.
参考文献
| [1] | Eickemeyer J.;Selbmann D.;Opitz R.;Wendrock H.;Maher E.;Miller U. Prusseit W. .Highly cube textured Ni-W-RABiTS tapes for YBCO coated conductors[J].Physica, C. Superconductivity and its applications,2002(Pt.2):814-817. |
| [2] | 赵跃,索红莉,刘敏,何东,祝永华,高忙忙,周美玲.涂层导体金属基带的研究进展[J].中国有色金属学报,2008(03):457-464. |
| [3] | Suenaga, M;Iwakuma, M;Sueyoshi, T;Izumi, T;Mimura, M;Takahashi, Y;Aoki, Y .Effects of a ferromagnetic substrate on hysteresis losses of a YBa2Cu3O7 coated conductor in perpendicular ac applied magnetic fields[J].Physica. C, Superconductivity and its applications,2008(15/20):1714-1717. |
| [4] | Kim YH;Sung TH;Han SC;Han YH;Jeong NH;Kim CJ;Jun BH;Oh SS;Kim HS;Kim TH .Factors associated with biaxial texturing of Cu tapes for YBCO coated conductors[J].Physica, C. Superconductivity and its applications,2007(0):625-629. |
| [5] | Jin M.;Sung T.;No K.;Han S. .Biaxial texturing of Cu sheets and fabrication of ZrO2 buffer layer for YBCOHTS films[J].Physica, C. Superconductivity and its applications,2000(3/4):243-248. |
| [6] | Adamik M.;Tomov I.;Barna PB. .Correlation between texture and average grain size in polycrystalline Ag thin films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1):33-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%