利用多功能雾化沉积装置,制备了Ni3Al-Mo高温合金.拉伸性能测试表明:喷射沉积Ni3Al-Mo合金的屈服强度有明显的"R"特性,即喷射沉积合金的屈服强度随着温度的增加而增加,在760 ℃时达到最大值;随着温度的继续增加,屈服强度会逐渐降低.利用TEM对位错结构分析,阐明了合金屈服强度与微观结构之间的关系.研究结果表明,试验合金所具有的屈服强度随温度的变化规律主要是由不同温度下γ′及γ相内的位错缠结状况、位错对的形态及数量和六面体滑移系的开动程度决定的.裂纹的TEM分析表明,随着变形应力的增加,裂纹在晶界部位产生,然后迅速扩展,而且在不同的晶面内存在一些不同的滑移带.喷射沉积合金在室温、中温及高温下裂纹严格沿八面体滑移系(111)面开裂.
A Ni3Al-Mo intermetallic compound alloy (IC6) was prepared by using the multifunctional spray atomization and deposition plant. Tensile properties tests indicate that the spray deposited Ni3Al-Mo alloy possesses "R" characteristics in the yield strength, that is, the yield strength of the spray deposited IC6 increases with increasing of temperature and it reaches maximum around 760 ℃. After that, they decrease with increasing of temperature. Analyses of dislocation structure by TEM reveal the relationship between the microstructure and yield strength. The results show that the change of the yield strength of the alloy with temperature is associated with the condition of dislocation winding, pattern and quantity of the dislocation pairs and starting degree of the hexahedron slip system inside γ′ and γ phases. The analysis of cracking by stereographic projection shows that with the increase of deformation stress the cracks form at grain boundaries and then quickly propagate, and some different slip bands exist in little planar zones; no matter at room temperature, middle temperature or high temperature, cracks craze along (111) plane octahedron slip.
参考文献
| [1] | Pope D P;Ezz S S .[J].International Metals Reviews,1984,29:136. |
| [2] | Copley S M;Kear B H .[J].Transactions TMS-AIME,1967,237:977. |
| [3] | Thkeuchi S;Kuramoto E .[J].Acta Metallurgy,1973,237:977. |
| [4] | 姚学兴 .延性L1<,2>型金属间化合物(Fe,Co,Ni)<,3>V系的微观设计及其形变断裂研究[D].清华大学,1990. |
| [5] | 米国发;罗治平;田世藩 .[J].金属学报,1997,33(06):566. |
| [6] | 米国发.喷射沉积IC6合金的拉伸性能及断裂特征[J].材料工程,1997(07):14. |
| [7] | 米国发 .喷射沉积Ni-Al-No系Mi<,3>Al基高温合金及其复合材料研究[D].哈尔滨工业大学,1995. |
| [8] | 刘文西;黄孝瑛;陈玉如.材料结构电子显微分析[M].天津:天津大学出版社,1988 |
| [9] | 黄孝瑛.电子显微分析[M].北京:机械工业出版社,1987 |
| [10] | Hersh P;Hoy A;Nicolson R B;刘永安 李永洪.薄晶体电子显微学[M].北京:科学出版社,1992 |
| [11] | 郭可信;叶恒强;吴玉琨.电子衍射图在晶体学中的应用[M].北京:科学出版社,1983 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%