为了提高6063铝合金的防腐蚀性能,制备了一种6063铝合金苯胺(BAN)封闭膜.采用极化曲线及交流阻抗技术研究了不同体积分数苯胺所制备的封闭膜的电化学性质.与去离子水中的封闭膜及基体的铝合金相比,极化曲线结果表明当苯胺的体积分数为0.12％ ～0.42％时,生成的苯胺封闭膜具有较正的点腐蚀电位及较低的腐蚀电流;交流阻抗谱数据也显示当苯胺的体积分数为0.12％～0.42％时,封闭膜具有较高的腐蚀阻抗,说明苯胺封闭膜具有较好的耐腐蚀性能.全浸失质量速率测试结果也表明苯胺封闭膜对6063铝合金有一定的防护作用.采用扫描电镜对样品的表面形貌进行了测试,测试结果与其电化学现象一致.
参考文献
| [1] | TRDAN U;GRUM J.Evaluation of corrosion resistance of AA6082-T651 aluminium alloy after laser shock peening by means of cyclic polarisation and ElS methods[J].Corrosion Science,2012(59):324-333. |
| [2] | 孔祥峰,任广军.铝合金磷化工艺的研究[J].电镀与精饰,2010(07):32-34. |
| [3] | Yin, Z.;Chen, F..Effect of nickel immersion pretreatment on the corrosion performance of electroless deposited Ni-P alloys on aluminum[J].Surface & Coatings Technology,2013:34-40. |
| [4] | CK. Chung;M.W. Liao;H.C Chang;C.T. Lee .Effects of temperature and voltage mode on nanoporous anodic aluminum oxide films by one-step anodization[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2011(5):1554-1558. |
| [5] | 娄淑芳,李红玲.无铬磷酸盐稀土转化膜工艺研究[J].涂料工业,2011(01):38-43. |
| [6] | 梁永煌,满瑞林,肖围,宋维鑫.铝管表面有机硅烷及其掺杂钝化研究[J].涂料工业,2010(10):61-65. |
| [7] | 刘建华,盛华,李明,李松梅,于美.三种有机物对LY12CZ铝合金在酸性溶液中的缓蚀行为研究[J].材料工程,2011(05):41-47. |
| [8] | Pardo A;Merino MC;Arrabal R;Merino S;Viejo F;Carboneras M .Effect of Ce surface treatments on corrosion resistance of A3xx.x/SiCp composites in salt fog[J].Surface & Coatings Technology,2006(9):2938-2947. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%