采用溶胶-冷冻干燥法制备了La1-xBaxCo0.8Ni0.2O3(x=0～0.4)催化剂粉体.用X射线衍射(XRD)、比表面测定仪(BET)和扫描电子显微镜(SEM)等分析手段对催化剂的结构和形貌进行了表征,并考察了催化剂的最佳焙烧温度和催化活性.研究表明,催化剂的最佳焙烧温度为600℃.掺杂Ba2+后,催化剂以钙钛矿相和BaCO3相共存,不能形成单一的钙钛矿型结构.催化活性测试表明,当x=0.2时,催化剂对CO的催化活性最高(T90%=126℃).
参考文献
| [1] | Liu Yuan;Zheng Haitao;Liu Jinrong .Preparation of high surface area La1-xAxMnO3(A=Ba,Sr or Ca)ultra-fine particles used for CH4 oxidation[J].Chemical Engineering Journal,2002,89:213. |
| [2] | Bakul Pant;Susan M.Stagg-Williams .Investigation of the stability of Pt/LaCoO_3 during high temperature reforming reactions[J].Catalysis Communications,2004(6):305-309. |
| [3] | Sina Sartipi;Abbas Ali Khodadadi;Yadollah Mortazavi .Pd-doped LaCoO3 regenerative catalyst for automotive emissions control[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2008(3/4):214-220. |
| [4] | 王海,朱永法,谭瑞琴,曹立礼.非晶态配合物法制备钙钛矿型纳米粉体催化剂及其CO催化氧化性能[J].化学学报,2003(01):13-16. |
| [5] | 白雪,刘源,王晓燕,张通,于文国.La1-x-yBaxREyMnO3（RE：Dy,Y）超细粒子的制备和其对CH4燃烧的催化性能[J].中国稀土学报,2004(04):561-566. |
| [6] | Huang Haifeng;Liu Yaqin;Tang Wei;Chen Bifen .Catalytic activity of nanometer La1-xSrxCoO3(x=0,0.2)perovskites towards VOCs combustion[J].Catalysis Communications,2008,9:55. |
| [7] | 李彦,余春江,骆仲泱,许祝安,岑可法.复合掺杂氧化物La0.5Sr0.5CoO2.91的性能和稳定性[J].中国稀土学报,2006(04):442-446. |
| [8] | 雷泽,朱庆山.纳米La0.6Sr0.4Co0.2Fe0.8O3-δ阴极粉体的溶液燃烧法合成与性能表征[J].物理化学学报,2007(02):232-236. |
| [9] | 杨立滨,井立强,李姝丹,蒋保江,付薇,付宏刚.ABO3型钙钛矿结构的可见光光催化剂LaCo0.5Ti0.5O3的设计与合成[J].高等学校化学学报,2007(03):415-418. |
| [10] | 廖润华,李月明,张玉平,江向平.溶胶-凝胶法合成（Na0.5Bi0.5）TiO3微粉[J].硅酸盐通报,2006(06):72-75,158. |
| [11] | 刘伟,罗来涛,吴跃辉.大比表面积La0.8Sr0.2CoO3的制备及甲烷催化燃烧性能研究[J].中国稀土学报,2008(02):135-140. |
| [12] | 侯磊,侯育冬,宋雪梅,朱满康,汪浩,严辉.水热法合成K0.5Bi0.5TiO3纳米陶瓷粉体[J].无机化学学报,2006(03):563-566. |
| [13] | 徐菁利,李树本,李茸,马建泰,任家荣,兰劲松.稀土钙钛矿型催化剂对CO催化氧化活性及表面氧种的研究[J].环境工程,2000(05):57-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%