通过热疲劳试验评价了H13钢硬度对其热疲劳行为的影响.同时,建立多场耦合数值模型研究热循环过程中H13钢的温度演变规律及应力累积过程,并进行寿命预测.试验结果表明,硬度为46 HRC试样的热疲劳损伤因子最小,抗热疲劳性能最佳.数值结果表明,在感应加热阶段,试样中心截面形成两个对称分布的弯月形高温区;在空冷均温阶段,弯月形高温区将向心部扩展;空冷结束时,中心截面上高温区位于表面和心部之间.不同硬度试样随热循环次数的增加其等效应力呈现累积效应,尤其在热疲劳裂纹形成部位,硬度为46 HRC试样的等效应力值最小,累积速率最慢,热疲劳寿命最高.
参考文献
| [1] | D. Klobcar;L. Kosec;B. Kosec.Thermo fatigue cracking of die casting dies[J].Engineering failure analysis,2012:43-53. |
| [2] | A. Persson;S. Hogmark;J. Bergstrom.Temperature profiles and conditions for thermal fatigue cracking in brass die casting dies[J].Journal of Materials Processing Technology,20042(2):228-236. |
| [3] | C. Gardin;Hoai Nam Le;G. Benoit;D. Bertheau.Crack growth under thermal cyclic loading in a 304L stainless steel - Experimental investigation and numerical prediction[J].International Journal of Fatigue,201010(10):1650-1657. |
| [4] | Szmytka, F.;Salem, M.;Rezai-Aria, F.;Oudin, A..Thermal fatigue analysis of automotive Diesel piston: Experimental procedure and numerical protocol[J].International Journal of Fatigue,2015:48-57. |
| [5] | 吴晓春;许珞萍.模具钢热疲劳裂纹的计算机辅助评定[J].上海金属,2001(6):1-5. |
| [6] | Hong Yan;J. Hua;R. Shivpuri.Flow stress of AISI H13 die steel in hard machining[J].Materials & Design,20071(1):272-277. |
| [7] | 胡心彬 .铌微合金化H13钢的热疲劳行为[D].上海大学,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%