植酸是从谷类作物中提取的无毒有机磷酸化合物,由于它可迅速与Ca2+,Mg2+,Fe2+和Zn2+等金属离子结合形成螯合物,因此可用于金属的防护.植酸转化膜是一种环境友好型的镁合金表面处理方法,综述了镁合金表面植酸转化膜的研究进展.
参考文献
| [1] | Mordike B L;Ebert T .Magnesium properties application potential[J].Materials Science and Engineering A,2001,A302:37-45. |
| [2] | 张津;章宗和.镁合金及应用[M].北京:化学工业出版社,2004:283-307. |
| [3] | 曾荣昌,柯伟,徐永波,韩恩厚,朱自勇.Mg合金的最新发展及应用前景[J].金属学报,2001(07):673-685. |
| [4] | Ambat R.;Zhou W. .Electroless nickel-plating on AZ91D magnesium alloy: effect of substrate microstructure and plating parameters[J].Surface & Coatings Technology,2004(2/3):124-134. |
| [5] | Vuorilehto K. .An environmentally friendly water-activated manganese dioxide battery[J].Journal of Applied Electrochemistry,2003(1):15-21. |
| [6] | Bengston J;Wojtaszek M;Wojcik G et al.Mangnesium conversion coating composition and method of using same[P].US,6692583,2004-02-17. |
| [7] | 大下贤一郎;本泽正博 .镁合金的表面处理方法及镁合金构件[P].中国,1317598,2002-03-31. |
| [8] | 胡会利,程瑾宁,李宁,王雅芬.植酸在金属防护中的应用现状及展望[J].材料保护,2005(12):39-43. |
| [9] | 崔秀芳,李庆芬.镁合金表面植酸转化膜研究Ⅰ植酸转化膜成膜机理与耐蚀性研究[J].腐蚀科学与防护技术,2007(03):203-206. |
| [10] | 崔秀芳,李庆芬.镁合金表面植酸转化膜研究Ⅱ.pH值对镁合金植酸转化膜的影响[J].腐蚀科学与防护技术,2007(04):275-277. |
| [11] | 陈东初,吴建峰,龚伟慧,李文芳,徐东明.AZ91D镁合金表面植酸转化膜的正交实验优化研究[J].兵器材料科学与工程,2009(02):4-8. |
| [12] | 郑润芬,梁成浩,邵林.AZ91D镁合金植酸转化膜组成与耐蚀性能研究[J].大连理工大学学报,2006(01):16-19. |
| [13] | 张华云,李华伦,郭伊娜.镁合金化学转化膜的耐腐蚀性研究[J].材料保护,2007(01):10-12. |
| [14] | 林继兴,牛丽媛,高光亮,刘兰云,李勇.镁表面防腐蚀植酸处理方法[J].轻合金加工技术,2008(09):36-39. |
| [15] | 柏冬.pH值对植酸络合能力的影响[J].山东师范大学学报（自然科学版）,2004(02):104-105,109. |
| [16] | Liu JR;Guo YN;Huang WD .Study on the corrosion resistance of phytic acid conversion coating for magnesium alloys[J].Surface & Coatings Technology,2006(3/4):1536-1541. |
| [17] | Zhang R F;Zhang S F;Duo S W .Influence of phytic acid concentration on coating properties obtained by MAO treatment on magnesium alloys[J].Surface and Coatings Technology,2009,255:7893-7897. |
| [18] | Xiufang Cui;Qingfen Li;Ying Li;Fuhui Wang;Guo Jin;Minghui Ding .Microstructure And Corrosion Resistance Of Phytic Acid Conversion Coatings For Magnesium Alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2008(5P1):2098-2103. |
| [19] | Shimakura;Toshiaki;Sasaki et al.Non-chromate metallic surface-treating agent,method for surface treatment,and treated steel material[P].US,6475300,2002-11-05. |
| [20] | Shimakura;Toshiaki;Sasaki .Method for treating metallic surface[P].US,6572983,2003-06-03. |
| [21] | Wippermann K;Scuize J W;Kessel R et al.The inhibition of zinc corrosion by bisanunotriazole and orther triazole teribatives[J].Corrosion Science,1991,32(02):205-207. |
| [22] | Manov S;Lamazouere A M;Aries L .Electrochemical study of the corrosion behaviour of zinc treated with a new orgaic chelating inhibitor[J].Corrosion Science,2000,42(05):1235-1248. |
| [23] | Mysliczyk;Richard G;Mccarty et al.Epoxy resin based coating composition and method[P].US,5635049,1997-06. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%