首先合成了含硅氧烷基的芳香亚胺封端剂N-苯亚甲基-3-三乙氧基硅烷基-1-丙胺(TEOS),然后用负离子原位聚合法合成了端基官能化聚苯乙烯PS-TEOS.采用红外光谱、核磁共振和凝胶渗透色谱对TEOS和PS-TEOS的结构进行了表征.研究了TEOS与聚苯乙烯基锂的定量反应关系,以及TEOS加入量、反应温度、反应时间及PS相对分子质量对封端效率的影响.结果表明,封端反应在10 min～5 min内快速完成,封端反应温度在55℃～80℃、PS的(M)n在5000～50000范围内变化对封端效率影响不大,制备的PS-TEOS的官能度在80％以上,实现了TEOS与聚苯乙烯基锂等摩尔封端反应.
参考文献
| [1] | Hirao A.;Haraguchi N.;Hayashi M. .Synthesis of well-defined functionalized polymers and star branched polymers by means of living anionic polymerization using specially designed 1,1-diphenylethylene derivatives[J].Macromolecular rapid communications: Publishing the newsletters of the European Polymer Federation,2000(17):1171-1184. |
| [2] | Quirk RP;Kim H;Polce MJ;Wesdemiotis C .Anionic synthesis of primary amine functionalized polystyrenes via hydrosilation of allylamines with silyl hydride functionalized polystyrenes[J].Macromolecules,2005(19):7895-7906. |
| [3] | 薛宏,赵万才,张春庆,计福春,刘青.n-BuLi/THF体系希夫碱末端化学改性SSBR的研究[J].弹性体,2001(04):5-7. |
| [4] | 郑仰才 .官能化SBS的合成及其应用[D].大连理工大学,2007. |
| [5] | Wang Q;Liao MY;Wang YR;Ren Y .Characterization of end-functionalized styrene-butadiene-styrene copolymers and their application in modified asphalt[J].Journal of Applied Polymer Science,2007(1):8-16. |
| [6] | 廖明义,郑仰才,金美花.以西弗碱为封端剂原位合成官能化苯乙烯-丁二烯-苯乙烯嵌段共聚物[J].合成橡胶工业,2008(02):109-112. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%