利用超音速等离子喷涂在调质45钢基体上制备了BaTiO3涂层,运用SEM、XRD、XPS等分析手段对所制备的涂层的组织形貌、物相成分及元素价态进行表征及分析；并利用显微硬度仪和纳米压痕仪对涂层的力学性能进行了表征.结果表明,BaTiO3涂层表面为灰白色,涂层光滑平整,孔隙率为0.8％；涂层为典型的层状结构,基体与BaTiO3涂层间的结合为机械结合,平均值为42MPa;纳米压痕仪测量涂层的表面硬度为7.065GPa,弹性模量为103.77GPa,显微硬度达到648.6HV0.1,涂层显示出优良的机械性能；XRD衍射结果显示主要成分为BaTiO3相,衍射峰的晶面指数为(101)、(111)和(200).通过超音速等离子喷涂制备的涂层可以获得较好的综合性能.
参考文献
| [1] | 徐滨士.再制造工程基础及其应用[M].哈尔滨:哈尔滨工业大学出版社,2005 |
| [2] | 王海军.热喷涂工程师指南[M].北京:国防工业出版社,2010 |
| [3] | Hiramatsu T;Tamura T;Wada N;Tamura H;Sakabe Y .Effects of grain boundary on dielectric properties in fine-grained BaTiO3 ceramics[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2005(1/3):55-58. |
| [4] | Pavel Ctibor;Helene Ageorges;Josef Sedlacek;Radim Ctvrtlik .Structure and properties of plasma sprayed BaTiO_3 coatings[J].CERAMICS INTERNATIONAL,2010(7):2155-2162. |
| [5] | Dent A H;Patel A;Gutleber J et al.High velocity oxy-fuel and plasma deposition of BaTiO3 and (Ba,Sr)TiO3[J].Ma terials Science and Engineering B,2001,87:23-30. |
| [6] | 王海军.热喷涂材料[M].北京:国防工业出版社,2010 |
| [7] | 张文峰,燕青芝,宿新泰,葛昌纯.制粉工艺对钛酸钡性能的影响[J].功能材料,2005(11):1734-1736. |
| [8] | 谢存毅.纳米压痕技术在材料科学中的应用[J].物理,2001(07):432-435. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%