Spinel LiMn2O4 was synthesized by glycine-nitrate method and coated with CaCO3 in order to enhance the electrochemical performance at room temperature (25°C) and 55°C. The uncoated and CaCO3-coated LiMn2O4 materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. XRD and SEM results indicated that CaCO3 particles encapsulated the surface of the LiMn2O4 without causing any structural change. The charge-discharge tests showed that the specific discharge capacity fade of pristine electrode at 25 and 55°C were 25.5% and 52%, respectively. However, surface modified cathode shows 7.4% and 29.5% loss compared to initial specific discharge capacity at 70th cycle for 25 and 55°C, respectively. The improvement of electrochemical performance is attributed to suppression of Mn2+ dissolution into electrolyte via CaCO3 layer.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | Y.W. Tsai, R. Santhanam and B.J. Hwang: J. Power Sources, 2003, 119, 701.[2 ] D. Im and A.J. Manthiram: J. Electrochem. Soc., 2003, 150, A742.[3 ] J.M. Tarascon and D. Guyomard: Electrochim. Acta, 1993, 38, 1221.[4 ] S.B. Park, S.M. Lee, H.C. Shin and W.I. Cho: J. Power Sources, 2007, 166, 219.[5 ] K.Y. Chung, C.W. Ryu and K.B. Kim: J. Electrochem. Soc., 2005, 152, A791.[6 ] Y. Shao-horn, S.A. Hackney, A.J. Kahaian, K.D. Kepler, E. Skinner, J.T. Vaughey and M.M. Thackeray: J. Power Sources, 1999, 81-82, 496.[7 ] H. S» |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%