通过调整合金的组成,优化其熔炼和热处理过程,制备出一种新组成的富La贮氢合金La0.62Ce0.25Pr0.03Nd0.10Ni3.69Co0.71Mn0.34Al0.29Zr0.005,用扫描电镜、压力-恒温实验、X射线衍射、恒电流充放电和循环伏安扫描方法对合金进行了表征.结果表明:该合金为六方晶系的CaCu5型结构;高温下氢的吸脱附平台低,65℃时压力平台为0.1 MPa;初始容量高达335 mAh/g,2 C经500次循环后,容降仅为18.6%.
参考文献
| [1] | 胡子龙.贮氢材料[M].北京:化学工业出版社,2002:45. |
| [2] | Lin H C;Lin K M;Chou H T et al.[J].Journal of Alloys and Compounds,2003,358:281. |
| [3] | Vivet S;Joubert J M;Knosp B et al.[J].Journal of Alloys and Compounds,2003,356-357:779. |
| [4] | 任可,雷永泉,陈立新,张庆安,王启东.（LaxCe1-x）0.9（PrNd）0.1（NiCoMnAl）5贮氢合金结构和电化学性能的研究[J].稀有金属材料与工程,2001(02):141-144. |
| [5] | Li S;Pan G L;Gao X P et al.[J].Journal of Alloys and Compounds,2004,364:250. |
| [6] | Seo C Y;Choi S J;Choi J et al.[J].Journal of Alloys and Compounds,2003,350:324. |
| [7] | Kronberger H .[J].Journal of Alloys and Compounds,1997,253-254:87. |
| [8] | Deng B H;Li Y F;Wang R Q et al.[J].Electrochimica Acta,1999,44:2853. |
| [9] | 夏熙.中国MH/Ni电池的现状与发展方向[J].电池,2002(z1):76-79. |
| [10] | Guo J H;Jiang Z T;Duan Q S et al.[J].Journal of Alloys and Compounds,1999,293-295:821. |
| [11] | Seo C Y;Choi S J;Choi J et al.[J].International Journal of Hydrogen Energy,2003,28:967. |
| [12] | 胡子龙.贮氢材料[M].北京:化学工业出版社,2002:205. |
| [13] | Ma J X;Pan H G;Chen C P et al.[J].International Journal of Hydrogen Energy,2002,27:57. |
| [14] | Okada M;Kuriiwa T;Tamura T et al.[J].Journal of Alloys and Compounds,1999,293-295:130. |
| [15] | 马建新,潘洪革,李寿权,陈长聘.RE（NiCoMnAl）5电极合金中RE成分对微结构和电化学性能的影响[J].稀有金属材料与工程,2002(03):217-220. |
| [16] | 李平,王新林,赵韦人,吴建民.低钴无钴贮氢合金研究的进展[J].电池,2002(04):238-241. |
| [17] | 周增林,宋月清,崔舜,杜军,康志君.高倍率AB5型稀土贮氢合金的研究进展[J].稀有金属,2004(02):408-413. |
| [18] | Seo C Y;Choi S J;Choi J et al.[J].International Journal of Hydrogen Energy,2003,28:317. |
| [19] | Nomuram K;Uruno H;Ono S .[J].Journal of the Less-Common Metals,1985,107(1-2):221. |
| [20] | 吴建民,杨素媛,李蓉,周少雄.退火对富铈Mm（NiCoMnAl）5储氢合金电化学性能的影响[J].中国稀土学报,2003(06):725-728. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%