通过溶胶凝胶法制备了不同掺杂浓度的Ag/CoO纳米复合薄膜.利用DTA-TG研究了CoO干凝胶的分解温度和分解产物,初步确定了退火温度为600 ℃,气氛为N_2.X射线衍射分析表明:薄膜中存在Ag和CoO两相.在300~800 nm范围内的吸收光谱表明,Ag/CoO复合薄膜在410 nm波长左右出现显著的表面等离子共振吸收峰,并且随着Ag含量的增加,吸收峰不断增强,其吸收峰位先蓝移后红移.当Ag含量(质量分数,下同)为40%时,吸收峰最强,继续增加Ag的含量,吸收峰强度开始下降.计算光学带隙,证明并解释了吸收峰移动.

Ag-doped CoO nanocomposite films have been synthesized by Sol-Gel. DTA-TG was used to determine the decomposition temperature and decomposition product of the CoO xerogel. X-ray diffraction analysis indicated that both CoO and metal Ag phases existed. The optical absorption measured in the range of 300 to 800 nm showed that the Ag/CoO films have obvious surface plasmon resonance peak at the wavelength of around 414nm. With increasing Ag content, the absorption the intensity of the peak increases, and absorption peak blue-shifted first and then red-shifted. When Ag content is 40%, the absorption peaks show the largest intensity, then the intensity decreases. Optical band gap was calculated and explained the shifting behavior of absorption peaks.

参考文献

[1] Ramnai S P;Jayashri Biswal .[J].Radiation Physics and Chemistry,2007,76:1290.
[2] Yang Lin;Liu Yuliang .[J].Microelectronic of Engineering,2003,66:192.
[3] Abeles B;Priestlry E B;Cohen R W .[J].Physical Review B:Condensed Matter,1975,12(06):121.
[4] Liao H B;Wong Weijia .[J].Journal of Applied Physics,2003,93(08):4485.
[5] Yang G;Wang W T;Zhou Y L .[J].Applied Physics Letters,2002,81(21):3969.
[6] Powell R J;Spicer W E .[J].Physical Review B,1970,2(06):2182.
[7] 李丽君,吴锦雷.金属微粒-介质复合薄膜(Au-BaO,Cu-BaO)的光吸收[J].物理学报,1998(05):790-795.
[8] Yoshihiko Takeda;Oleg Plaksin A .[J].Vacuum,2006,80:776.
[9] Fantini MCA.;Ferreira FF.;Gorenstein A. .Theoretical and experimental results on Au-NiO and Au-CoO electrochromic composite films[J].Solid state ionics,2002(Pt.A):867-872.
[10] 张波萍,焦力实,张芸,李向阳.金属纳米颗粒分散氧化物Au/SiO2薄膜的制备与光吸收特性[J].稀有金属材料与工程,2005(z2):990-993.
[11] Laureti S;Agostinelli E;Scavia G .[J].Applied Surface Science,2008,254:5111.
[12] Enrique Barrera;Tomas Viveros;Alejandro Avila;Patricia Quintana;Miguel Morales;Nikola Batina .Cobalt oxide films grown by a dipping sol-gel process[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(1/2):138-144.
[13] 张克立,贾漫珂,汤昊,郭光辉.乙酸钴热分解机理研究[J].武汉大学学报(理学版),2002(04):409-412.
[14] Shanmugam Yuvaraj;Lin Fanyuan .[J].Journal of Physical Chemistry B,2003,107:1044.
[15] Pan A L;Zheng H G et al.[J].Materials Research Bulletin,2003,38:789.
[16] Raffi M;Akhter JI;Hasan MM .Effect of annealing temperature on Ag nano-composite synthesized by sol-gel[J].Materials Chemistry and Physics,2006(2/3):405-409.
[17] Patil PS.;Lokhande CD.;Kadam LD. .PREPARATION AND CHARACTERIZATION OF SPRAY PYROLYSED COBALT OXIDE THIN FILMS[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1996(1):29-32.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%