环境促进开裂中裂纹扩展速度的测定方法述评

中国腐蚀与防护学报, 1998, 18(3): 214-220.

环境促进开裂中裂纹扩展速度的测定方法述评

牛林 , 林海潮 , 曹楚南 , 宋光铃 , 史志明

中国科学院金属腐蚀与防护研究所

金属腐蚀与防护国家重点实验室沈阳110015

中国科学院金属腐蚀与防护研究所

金属腐蚀与防护国家重点实验室沈阳110015

中国科学院金属腐蚀与防护研究所

金属腐蚀与防护国家重点实验室沈阳110015

中国科学院金属腐蚀与防护研究所

金属腐蚀与防护国家重点实验室沈阳110015

中国科学院金属腐蚀与防护研究所

基金项目: 国家自然科学基金；中国科学院“百人计划”资助项目

关键词：裂纹扩展速度 , Environmentally assisted cracking , Method

EVALUATION OF DETERMINATION METHODS OF CRACK PROPAGATION RATE IN ENVIRONMENTALLY ASSISTED CRACKING

NIU Lin LIN Hai-chao CAO Chu-nan SONG Guang-ling SHI Zhi-ming(The Institute of Corrosion and Protection of Metals , Chinese Academy of Sciences , State Key Laboratory of Corrosion and Protection , Shenyang 110015) , null

Keywords： Crack propagation rate , 环境促进开裂 , 方法

文中综述了环境促进开裂中几种有代表性的裂纹扩展速度的确定方法及有关模型,并对这些方法和模型的使用范围及其优缺点进行了分析和评价。

The determination methods and relevant models of crack propagation rate in environmentally assisted cracking were summed up and reviewed. The advantages and shortcomings as well as application range of these methods and models were analyzed and evaluated. The main purpose of the review was to provide convincing basis not only for the most suitable determination of crack propagation rate in various complex material/environment combinations but also for the life-prediction of components in practical service.

参考文献

[1]	Brown B F. Stress Corrosion Cracking in High Strength Steels, and in Titanium and Aluminum Alloys, NRL, Washington D C. 1972
[2]	Chu W, Hsiao C, Tu S, et al. Corrosion, 1982, 38:446
[3]	Wendier-Kalsch E. Werkstoffe and Corrosion, 1978, 29:703
[4]	Speidel M O. Corrosion, 1977, 33:199
[5]	Haruna T, Shibata T. Corrosion, 1994, 50:785
[6]	Speidel M O. Metall. Trans. A, 1981, 12A: 779
[7]	Speidel M O. The Theory of Stress Corrosion Cracking in Alloys, eds. Scully J C, NATO, Scientific Affairs Division, Brussels, 1971. p289
[8]	Parking R N. Brit. Corros. J., 1979, 14:5
[9]	Ford F P. Corrosion Processes, eds. Parkins R N, Applied Science, New York, NY, 1982. p271
[10]	Ford F P. EPRI Report NP2589, Palo Alto, CA: EPRI, 1982
[11]	Ford F P, et al. Corrosion/85, Paper no. 352, Boston, 1985
[12]	Ford F P. Corrosion/86, Paper no. 327, Houston, 1986
[13]	Parkins R N. Proc. 3rd Int. Conf. Mechanical Behavior of Materials, Cambridge, U. K, August 1979, eds. K. J. Miller et al., Pergamon Press, 1980. p139
[14]	Ford F P. Corrosion, 1996, 52:375
[15]	Congleton J, et al. Corros. Sci., 1985, 25:633
[16]	Parkins R N, et al. Metal Sci., 1977, 11:405
[17]	Parkins R N. Corrosion, 1990, 46:178
[18]	Turnbull A. Corros. Sci., 1993, 34:921
[19]	Parkins R N. Environment-induced Cracking of Metals, eds. Gangloff R Petal., NACE, Houston,1990, pl
[20]	Scully J C. Corros. Sci., 1968, 8:513
[21]	Parkins R N. Corros. Sci., 1980, 20:147
[22]	Jones D A. Metall. Trans. A, 1985, 16A: 1133
[23]	Ford F P, Burstein G T, Hoar T P. J.Electrochem. Soc., 1980, 127:6
[24]	Hagyard T, Earl W B. J. Electrochem. Soc., 1968, 115:623
[25]	Less D J, Hoar T P. Corrs. Sci., 1980, 20:723
[26]	Newman R C, Burstein G T. Corros. Sci., 1981, 21:119
[27]	Diegle R B, Lineman D M. J. Electrochem. Soc., 1984, 131:106
[28]	Diegle R B, Vermilyea D A. J. Electrochem. Soc., 1975, 122:180
[29]	Ford F P, Silverman M. Corrosion, 1980, 36:558
[30]	Carranza R M, Galvele J R. Corros. Sci., 1988, 28:233
[31]	Carranza R M, Galvele J R. Corros. Sci., 1988, 28:851
[32]	Galvele J R, Torresi R M, Caxrauza R M. Corros. Sci.,1990, 31:536
[33]	Beck T R. J. Electrochem. Soc., 1982, 129:2500
[34]	Beck T R. Corrosion, 1974, 30:408
[35]	Wei R P, Alavi A. Scrip. Metall. 1988, 22:969

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网