利用声发射技术对45钢马氏体相变过程进行了监测，通过采集连续冷却条件下马氏体相变的声发射信号，并结合信息熵理论对45钢马氏体相变温度进行了测定。结果表明：利用信息熵理论测定的45钢马氏体相变开始温度为335．7℃，与实际相度温度的误差为1．26％。
Using acoustic emission technology to monitor the martensite transformation process of 45 steel. The acoustic emission signal of martensite phase transformation was collected under continuous cooling condition, and according to the information entropy theory, the martensite phase transformation temperature of 45 steel was determined. The result show that the martensite phase transformation starting temperature of 45 steel determined using information entropy theory was 335. 7 ℃, and ,the error rate was 1. 26% comparing with the actual phase transformation temperature.
参考文献
| [1] | 潘红波,唐获,胡水平,王潇潇,丁勇生.热分析法测量相变温度的研究[J].物理测试,2008(06):43-46. |
| [2] | 甄睿.形状记忆合金相变温度的常用测量方法[J].南京工程学院学报（自然科学版）,2006(01):27-32. |
| [3] | 戴光.声发射检测技术在中国--庆祝中国机械工程学会无损检测分会成立三十周年[J].无损检测,2008(07):389-396. |
| [4] | 刘浩广,蔡绍洪.信息熵及其随机性[J].贵州大学学报（自然科学版）,2007(04):350-351,356. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%