在实验室φ450 mm轧机上用控制轧制和控制冷却的方法制备了X80管线钢板,采用光学显微镜、透射电镜和力学性能试验机等研究了卷取温度对该钢显微组织和力学性能的影响.结果表明:当卷取温度在463～597℃范围内变化时,随着卷取温度的升高,该钢组织中针状铁素体含量增加,M-A岛更细小均匀,显微组织明显细化;在597℃卷取时,该钢的屈服强度达到650 MPa,抗拉强度达到790 MPa,伸长率达到30%左右.
X80 pipeline steel plate was prepared by controlled rolling and controlled cooling method using a φ 450 mm laboratory rolling mill The influence of coiling temperature on the microstrueture and mechanical properties of the steel was investigated by means of optical microscope,TEM and mechanical property tester.The results show that when the coiling temperature increased from 463 ℃ to 597 ℃,the content of acicular fertile (AF) in X80 pipeline steel increased,and the M-A island became finer and well-proportioned.When the coiling temperature was 597 ℃,the yield strength and tensile strength of X80 pipeline steel could be 650 MPa and 790 MPa respectively,and the elongation was about 30%.
参考文献
| [1] | 王仪康,潘家华,杨柯,单以银.高性能输送管线钢[J].焊管,2007(01):11-16. |
| [2] | C. Garcia de Andres;M.J. Bartolome;C. Capdevila .Metallographic techniques for the determination of the austenite grain size in medium-carbon microalloyed steels[J].Materials Characterization,2001(5):389-398. |
| [3] | 刘勤博,张红梅,汪红绢,刘振宇,王国栋.控制轧制对管线钢X65组织细化的影响[J].热加工工艺,2007(16):1-3,6. |
| [4] | 郑磊,高珊.高韧性针状铁素体X80级管线钢的试制[J].焊管,2005(02):21-24. |
| [5] | 许洪汛,唐荻,江海涛,田志强,马小亮.X80管线钢组织性能研究[J].新技术新工艺,2008(09):76-78. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%