采用电子束焊连接,随后近等温锻造+梯度热处理的工艺加工Ti-24Al-15Nb-1.5Mo/TC11双合金盘,通过OM、SEM、TEM、XRD等研究双合金盘的焊接界面状况.结果表明,经此工艺加工的Ti-24A1-15Nb-1.5Mo/TC11双合金盘的高温拉伸性能较优,焊缝的高温强度大于TC11钛合金,但室温拉伸性能分散度较大.采用梯度热处理不能消除经50%变形的双合金盘的焊缝到TC11侧热影响区的晶界α相.焊缝区簇状α_2相的形成与在近等温锻造、梯度热处理加热保温过程中Al、Nb元素从α_2相中分离出来有关.
The Ti-24Al-15Nb-1.5Mo/TC11 dual alloy discs were joined by electron beam welding firstly, and then underwent near isothermal forging and gradient heat treatment. The welding interface state was investigated by OM, SEM, TEM and XRD. The results show that the elevated temperature properties of the dual alloy disc are better and the high temperature strength is larger than that of the TC11 alloy. However, the dispersion degree of tensile properties is larger at the room temperature. When the dual alloy disc is deformed by 50%, the a phase is distributed in the β phase grain boundary from welding seam to the heat-affected zone of TC11 alloy, which can not be eliminated by gradient heat treatment. The cluster α_2 phase in the welding seam area is formed, which is ascribed to the diffusion of the Al and Nb elements from the α_2 phase during near isothermal forging and gradient heat treatment.
参考文献
| [1] | Henderson M B;Hannis J;McColvin G.[A].Warrendale:TMS,2002:3. |
| [2] | David Furrer;George Groppi;Gene Bunge .FORGING THE FUTURE PART II[J].Advanced Materials & Processes,2005(6):43-45. |
| [3] | Mourer D P;Raymond E;Ganesh S.[A].Warrendale:TMS,1996:637. |
| [4] | Yao Z K;Guo H Z;Cui Z S.[A].Warrendale:TMS,2004:715. |
| [5] | 姚泽坤;张梅琳;梁新民 et al.[J].焊接学报,2004,61:25. |
| [6] | Yao Zekun;Liang Xinmin;Guo Hongzhen.[A].Warrendale:TMS,2004:445. |
| [7] | 姚泽坤,梁新民,郭鸿镇,陈绍楷,张会.热力因素对合金元素在Ti-24Al-15Nb-1.5Mo/TC4焊接界面上扩散规律的影响[J].稀有金属材料与工程,2005(06):907-911. |
| [8] | Bendersky L A;Boettinger W J;Roytburd A.[A].Sendai:JIM,1991:845. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%