为了研究ZL108铝合金微弧氧化膜的Na2MoO4改性机理,在添加5种不同浓度的Na2MoO4溶液中对其进行微弧氧化处理.利用扫描电镜(SEM)观察微弧氧化膜表面形貌,用能谱仪(EDS)分析截面Mo、O元素含量,用XPS测定Mo、O元素的价态,用X射线衍射仪(XRD)分析相组成,采用极化曲线评定耐蚀性.结果表明,微弧氧化电压随着Na2MoO4浓度的增加而下降.微弧放电区温度高于1823.84 K时,MoO2-开始转变形成MoO2,抑制了微弧氧化膜表面多孔层的形成,提高了膜层的致密性、厚度和耐蚀性.浓度的改变对相组成影响较小.
参考文献
| [1] | 张欣盟,陈东方,巩春志,杨士勤,田修波.添加K2ZrF6对LY12铝合金微弧氧化膜层结构调制及隔热性能影响[J].无机材料学报,2010(08):865-870. |
| [2] | Aytekin Polat;Murat Makaraci;Metin Usta .Influence of sodium silicate concentration on structural and tribological properties of microarc oxidation coatings on 2017A aluminum alloy substrate[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2010(2):519-526. |
| [3] | Tseng, C.-C.;Lee, J.-L.;Kuo, T.-H.;Kuo, S.-N.;Tseng, K.-H. .The influence of sodium tungstate concentration and anodizing conditions on microarc oxidation (MAO) coatings for aluminum alloy[J].Surface & Coatings Technology,2012(16):3437-3443. |
| [4] | 蒋百灵,赵仁兵,梁戈,李均明,袁芳.Na2WO4对铝合金微弧氧化陶瓷层形成过程及耐磨性的影响[J].材料导报,2006(09):155-157. |
| [5] | 郑宏晔,王永康,曹立,李炳生,韩高荣.Na2WO4对铝合金表面微弧氧化陶瓷层性能的影响[J].浙江大学学报（工学版）,2005(05):742-745. |
| [6] | 张永君,蒙继龙.铝合金表面微弧氧化-黑化一体化技术研究[J].材料科学与工艺,2007(05):705-708,712. |
| [7] | 梁戈,赵仁兵,蒋百灵.电解液参数对铝合金微弧氧化黑色陶瓷膜性能的影响[J].材料热处理学报,2006(05):91-94. |
| [8] | 王平,郭小阳,王斌,杨洁.NaAlO2含量对ZAISil2Cu2Mgl铝合金Na2SiO3微弧氧化陶瓷膜性能的影响[J].材料保护,2012(09):21-24. |
| [9] | 王颖辉,刘向东,张雅萍,吕凯,国春燕,陈伟东.含Li2CO3的电解液中形成ZAlSi12Cu2Mg1合金微弧氧化膜的表征[J].稀有金属材料与工程,2010(z1):305-310. |
| [10] | 李美栓,钱余海,辛丽.合金上氧化物的体积比的分析[J].腐蚀科学与防护技术,1999(05):284-289. |
| [11] | 徐爱菊,林勤,照日格图,贾美林,刘莲云.FTIR和XPS光谱分析Co-V-O催化剂的丙烷氧化脱氢活性氧物种[J].光谱学与光谱分析,2009(02):346-350. |
| [12] | 于凯,许淳淳.钼酸钠对铁质文物的缓蚀作用研究[J].北京化工大学学报(自然科学版),2004(04):41-44. |
| [13] | 王成,江峰,林海潮.LY12铝合金钼酸盐转化膜研究[J].稀有金属材料与工程,2003(02):130-133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%