采用丙烯酸酯单体与聚氯乙烯(PVC)通用树脂共混,通过原位聚合反应制备PVC基热塑性弹性体.研究了增塑剂邻苯二甲酸二辛酯(DOP)的用量、丙烯酸酯橡胶的种类及用量对PVC基热塑性弹性体力学性能、动态力学性能以及加工流变性能的影响.结果表明,随着DOP用量的增加,材料的断裂伸长率逐渐增加,而拉伸强度呈现下降趋势,每100份PVC树脂中DOP用量为50份左右时,材料的拉伸强度出现最小值.同时,实验所使用的丙烯酸酯橡胶玻璃化转变温度(Tg)越低,所制备的PVC基热塑性弹性体的断裂伸长率越大,加工流变性能越好,而材料的拉伸强度越低.

参考文献

[1] 赵瑞时.日本PVC类热塑性弹性体[J].世界橡胶工业,2006(01):37-40.
[2] Huang XW;Tian N;Wang TM;Wang K;Xue QJ .Friction and wear properties of NBR/PVC composites[J].Journal of Applied Polymer Science,2007(4):2565-2570.
[3] Ismail H;Supri;Yusof AMM .Blend of waste poly(vinylchloride) (PVCw)/acrylonitrile butadiene-rubber (NBR): the effect of maleic anhydride (MAH)[J].Polymer Testing,2004(6):675-683.
[4] Supri;Ismail H .Effects of dynamic vulcanization and glycidyl methacrylate on properties of recycled poly(vinyl chloride)/acrylonitrile butadiene rubber blends[J].Polymer Testing,2006(3):318-326.
[5] Tan KL;Li CX;Meng H;Wang ZH .Preparation and characterization of thermoplastic elastomer of poly(vinyl chloride) and chlorinated waste rubber[J].Polymer Testing,2009(1):2-7.
[6] 刘赞,陈占勋,赵磊.PVC基热塑性弹性体的制备[J].聚氯乙烯,2005(05):26-29.
[7] 牛晓伟,严长浩,鲁萍,吴德峰,陈晓松,张明.用转矩流变仪调节聚氯乙烯/废胶粉热塑性弹性体的加工配方[J].合成橡胶工业,2006(04):275-279.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%