利用Ag-28Cu合金钎焊复合制备Ag/Cu复合材料，经轧制加工成复合带材。悁究轧制变形和扩散退火对复合界面形貌、界面组织和性能的影响，以及界面元素扩散特征。结果表明，随着轧制变形量增加，Cu、Ag-28Cu 和 Ag 发生协调变形，复合界面由波浪形，转变成锯齿状，最后 Cu层整体向Ag层倾斜。随着加工率增加，Cu层硬度逐渐降低，Ag-28Cu层硬度显著升高，Ag层硬度不变。随着退火温度增加，界面组织逐渐长大粗化，复合层宽度增加。界面原子扩散行为主要是Cu原子向Ag中发生扩散，退火温度增加时，Ag-28Cu层中Cu原子向Ag侧逐渐减少，Ag层中的Cu原子含量增加，Cu和Ag层硬度没有发生变化，而Ag-28Cu层硬度逐渐降低。
The Ag/Cu composite fillet prepared using Ag-28Cu brazing, was rolled into composite strip. The effects of rolling and diffusion annealing on composite interface morphology, microstructure and properties of interface were studied. And the diffusion characteristics of elements on interface were investigated. The results show that with the increase of rolling reduction, the deforms of Cu, Ag-28Cu and Ag were resulted coordinately. The interface of composite turns into zigzag form wavy, Cu layer inclines to the Ag layer finally. With the increase of processing rate, the hardness of Cu layer decreases gradually, the hardness of Ag-28Cu layer elevates significantly, the hardness of Ag layer unchanged. As the annealing temperature increasing, the interface structure grow gradually and the width of composite layer increases. The behavior of interface atomic diffusion is that Cu atoms mainly diffuse to the Ag. With annealing temperature increasing, Cu atoms in Ag-28Cu layer to Ag side reduces gradually, but Cu atoms in Ag layer increases. As annealing temperature increasing, the hardnesses of Cu and Ag layer have not changed, while the hardness of Ag-28Cu layer is decreased gradually.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%