为了研究温度、变形速率对TC4焊接件的力学性能影响,分别采用100～800℃下变形速率为0.001,0.1,1和10 s-1的拉伸试验来表征焊接件的动态力学性能,并基于Johnson-Cook模型对相应变形速率下的屈服强度进行理论计算,而后比较了计算值和实验所测的数值,结果说明可以采用Johnson-Cook模型来表征焊接件的动态力学性能.
参考文献
| [1] | 束德林.Engineering Material Mechanical Properties(工程材料力学性能)[M].北京:机械工业出版社,2003:15. |
| [2] | 冯端.Physics of Metals(金属物理学第三卷)[M].北京:机械工业出版社,1999:354. |
| [3] | 范成磊,方洪渊,陶军,田应涛,黎明.随焊冲击碾压控制平面封闭焊缝残余变形研究[J].哈尔滨工程大学学报,2005(02):238-241. |
| [4] | 方洪渊;刘雪松;杨建国 et al.[P].中国专利:200610150852.4,2006. |
| [5] | 张勇,杨建国,李军,刘雪松,方洪渊.随焊冲击旋转挤压控制TC4薄板焊接失稳变形工艺[J].焊接学报,2011(01):85-88. |
| [6] | Blazynski T Z.Materials at High Strain Rates[M].New York:Elesevier Applied Science Publishers Ltd,1987:33. |
| [7] | Johnson G R;Cook W H.[A].Hague:EMAS,1983:541. |
| [8] | Macdougall, DAS;Harding, J .A constitutive relation and failure criterion for Ti6Al4V alloy at impact rates of strain[J].Journal of the Mechanics and Physics of Solids,1999(5):1157-1185. |
| [9] | Nemat Nasser;Guo S;Wei-Guo et al.[J].Experiments and Modeling Mechanics of Materials,2001,33(08):425. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%