根据X100管线钢断口分层现象,对该钢圆棒形及板形拉伸试样断口及不同温度下冲击试样断口进行宏观观察、显微分析、金相观察和EBSD织构分析.结果表明,随拉伸试样形状及尺寸的变化,裂纹分层现象趋势不同,随冲击试验温度降低,裂纹趋势加剧,裂纹的萌生以及扩展受晶界的限制.EBSD织构分析表明,沿{113}〈110〉方向,在一定微区存在较强的织构,促进了断口分层的产生.
参考文献
| [1] | 杨政,郭万林,董蕙茹,路民旭,赵新伟,罗金衡.X70管线钢冲击韧性实验研究[J].金属学报,2003(02):159-163. |
| [2] | 李文竹,庞兆夫,徐荣杰,王锐,王晓峰,苏国阳.管线钢DWTT分离断口的显微分析[J].物理测试,2007(04):47-51. |
| [3] | 杨政,任斌,赵新伟,霍春勇,郭万林.铁素体管线钢的分层裂纹及其对断裂的影响[J].材料研究学报,2007(03):311-318. |
| [4] | Sang Yong Shin;Byoungchul Hwang;Sunghak Lee;Nack J. Kim;Seong Soo Ahn .Correlation of microstructure and charpy impact properties in API X70 and X80 line-pipe steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):281-289. |
| [5] | Shin SY;Hwang B;Kim S;Lee S .Fracture toughness analysis in transition temperature region of API X70 pipeline steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):196-204. |
| [6] | B. Tanguy;T. T. Luu;G. Perrin;A. Pineau;J. Besson .Plastic and damage behaviour of a high strength X100 pipeline steel: Experiments and modelling[J].International Journal of Pressure Vessels and Piping,2008(5):322-335. |
| [7] | 于在松,范长信,刘江南,王弘喆,王正品,石崇哲.示波冲击试验中裂纹生长与扩展机理研究[J].铸造技术,2008(05):617-621. |
| [8] | 蓝慧芳,杜林秀,刘彦春,刘相华.控轧控冷工艺对高强度结构钢组织及力学性能的影响[J].东北大学学报（自然科学版）,2009(02):200-204. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%