研究了MgO-Al2O3-Re2O3(Re=Lu,Y)三元烧结助剂体系对无压烧结Si3N4陶瓷显微结构和力学性能的影响.研究结果表明,添加MgO-Al2O3-Lu2O3三元助剂制备的Si3N4陶瓷显微结构具有明显的双峰分布,晶粒较粗化,致密度、硬度、弯曲强度、断裂韧性分别为96.4％、14.59 GPa、964 MPa、7.64 MPa·m1/2;而添加MgO-Al2O3-Y2O3三元助剂制备的Si3N4陶瓷具有细化的显微结构,致密度、硬度、弯曲强度、断裂韧性分别为99.9％、15.29 GPa、758 MPa、6.60 MPa·m1/2.
参考文献
| [1] | Sampad K. Biswas;Frank L. Riley.Gas Pressure Sintering of Silicon Nitride Powder Coated with Al_2O_3 and TiO_2[J].Journal of the American Ceramic Society,20032(2):212-216. |
| [2] | Gayle S. Painter;Paul F. Becher.Bond Energetics at Intergranular Interfaces in Alumina-Doped Silicon Nitride[J].Journal of the American Ceramic Society,20021(1):65-67. |
| [3] | Hai-Doo Kim;Byung-Dong Han;Dong-Soo Park.Novel Two-Step Sintering Process to Obtain a Bimodal Microstructure in Silicon Nitride[J].Journal of the American Ceramic Society,20021(1):245-252. |
| [4] | Angel De Pablos;Joaquin Bermudo;Maria Isabel Osendi.Microstructure and Mechnical Properties of Silicon Nitride Materials Fabricated from SHS Powders[J].Journal of the American Ceramic Society,20015(5):1033-1036. |
| [5] | Yang J-F.;Ohji T..Influence of Yttria-Alumina Content on Sintering Behavior and Microstructure of Silicon Nitride Ceramics[J].Journal of the American Ceramic Society,20008(8):2094-2096. |
| [6] | Ling Gao;Haitao Yang;Runzhang Yuan.Sintering and microstructure of silicon nitride with magnesia and cerium additives[J].Journal of Materials Processing Technology,20013(3):298-301. |
| [7] | Paul F. Becher;Gayle S. Painter;Naoya Shibata.Effects of Rare-Earth (RE) Intergranular Adsorption on the Phase Transformation, Microstructure Evolution, and Mechanical Properties in Silicon Nitride with RE_2O_3+MgO Additives: RE = La, Gd, and Lu[J].Journal of the American Ceramic Society,20087(7):2328-2336. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%