选取具备我国典型热带海洋气候条件的万宁试验站,进行丙烯酸聚氨酯涂层(BDC)2 a近海大气的自然老化试验,对其在近海地区的老化历程及老化机理进行了研究;同时在实验室环境下进行了BDC样品的湿热、盐雾、UVA的循环老化试验,对其老化历程进行验证.结果表明:在万宁近海地区,BDC样品老化初期的光泽变化较明显,涂层以水解老化方式为主;老化中期涂层的失效大部分是由腐蚀介质Cl-的侵入而引起的;当老化1 a左右时,老化速度放缓,此时涂层的变化主要是由于光氧化作用;实验室加速循环试验谱湿热(168 h)-盐雾(168 h)-UVA(168 h)基本可以模拟涂层万宁近海地区1 a的变化,以色差为指标,模拟后关联度可达0.926,二者的XPS及FI-IR谱图也非常接近.
参考文献
| [1] | Aznar AC;Pardini OR;Amalvy JI.Glossy topcoat exterior paint formulations using water-based polyurethane/acrylic hybrid binders[J].Progress in Organic Coatings: An International Review Journal,20061(1):43-49. |
| [2] | 朱艳芳 .三种复合涂层失效过程的EIS研究及快速检测[D].北京化工大学,2010. |
| [3] | 杨丽霞 .丙烯酸聚氨酯和氟碳涂层老化对金属腐蚀的影响规律[D].北京科技大学,2006. |
| [4] | 潘莹;张三平;周建龙;李晓刚;王玲;萧以德.大气环境中有机涂层的老化机理及影响因素[J].涂料工业,2010(4):68-72. |
| [5] | 胡建文;高瑾;李晓刚;杜翠女.紫外光对丙烯酸聚氨酯清漆的老化影响规律研究[J].中国腐蚀与防护学报,2009(5):371-375. |
| [6] | 卢琳;胡建文;李晓刚;高瑾.光老化对丙烯酸聚氨酯/钢板界面附着力的影响[J].复合材料学报,2011(2):94-99. |
| [7] | Hu, JW;Li, XG;Gao, J;Zhao, QL.Ageing behavior of acrylic polyurethane varnish coating in artificial weathering environments[J].Progress in Organic Coatings: An International Review Journal,20094(4):504-509. |
| [8] | Merlatti C;Perrin FX;Aragon E;Margaillan A.Natural and artificial weathering characteristics of stabilized acrylic-urethane paints[J].Polymer Degradation and Stability,20085(5):896-903. |
| [9] | Sudeshna Saha;Duygu Kocaefe;Yaman Boluk;Andre Pichette.Surface degradation of CeO_2 stabilized acrylic polyurethane coated thermally treated jack pine during accelerated weathering[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013Jul.1(Jul.1):86-94. |
| [10] | Bhargava, S.;Kubota, M.;Lewis, R. D.;Advani, S. G.;Prasad, A. K.;Deitzel, J. M..Ultraviolet, water, and thermal aging studies of a waterborne polyurethane elastomer-based high reflectivity coating[J].Progress in Organic Coatings: An International Review Journal,2015:75-82. |
| [11] | 邓洪达;张三平;杨丽霞.不同地区大气曝晒对涂层耐蚀性能的影响Ⅰ.丙烯酸聚氨酯涂层[J].中国腐蚀与防护学报,2007(5):274-278. |
| [12] | Perrin FX.;Aragon E.;Vernet JL.;Irigoyen M..Artificial aging of acrylurethane and alkyd paints: a micro-ATR spectroscopic study[J].Polymer Degradation and Stability,20003(3):469-475. |
| [13] | 陈群志;孙祚东;陆维忠;韩恩厚;常铁军;李京.SEBF/SLF重腐蚀防护涂层应用于典型飞机结构中防腐性能综合评定[J].中国腐蚀与防护学报,2005(6):365-368. |
| [14] | 刘文珽;李玉海;陈群志;贺小帆.飞机结构腐蚀部位涂层加速试验环境谱研究[J].北京航空航天大学学报,2002(1):109-112. |
| [15] | 罗振华;蔡键平;张晓云;陆峰;姚琲.耐候性有机涂层加速老化试验研究进展[J].合成材料老化与应用,2003(3):31-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%