The double ellipsoidal model of heat source is used to analyze the thermal distributions with a three dimensional finite element method (FEM). In the mechanical model, solidification effects are treated by a dynamic element rebirth scheme. The driving force is obtained in the cracking susceptible temperature range. Moreover, this paper presents the effect of solidification shrinkage, external restraint, weld start locations and material properties on the driving force. The comparison between the simulated driving force and the experimental measurements of the material resistance predicts the susceptibility of weld metal solidification cracking.
参考文献
| [1] | Z L Feng .[D].Thesis Ohio State University,1993. |
| [2] | Y.H.Wei;R.P. Liu;Z.J.Dong .[J].China Welding,1999,8(02):135. |
| [3] | T Zacharia .[J].Welding Journal,1994,73(07):164. |
| [4] | D.Dye;O.Hunziker;R.C.Reed .[J].Acta Materialia,2001,49:683. |
| [5] | M Jonsson;L Karlsson;L E Lindgren.[A].Stockholm Sweden,1983 |
| [6] | Y Yang .[J].Welding Journal,2000,79(01):9. |
| [7] | Y Yang.[A].Pine Mountain,USA,1998 |
| [8] | W P Liu .[J].Computational Materials Science,1995,43(09):211. |
| [9] | Z·L·Feng;A·David;T·Zacharia et al.[J].Science and Technology of Welding and Joining,1997,2(01):11. |
| [10] | Y.H.Wei;R.P.Liu;Z.J.Dong .[J].China Welding,2000,9(01):36. |
| [11] | J Dike.[A].Gatlinburg,USA,1995 |
| [12] | J Goldak .[J].Metallurgical and Materials Transactions,1984,15B:587. |
| [13] | F Matsuda;H Nakagawa .[J].Transactions of JWRI(Joining and Welding Research Institute of Osaka University),1983,12(01):65. |
| [14] | F Matsuda;H Nakagawa .[J].Transactions of JWRI(Joining and Welding Research Institute of Osaka University),1983,12(01):73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%