采用激光燃烧合成技术，对掺杂钨精矿石粉末的钨精矿石／Al-Cu粉末压坯进行燃烧合成。采用SEM、OM、XRD以及维氏硬度计研究了钨精矿石粉末的含量对合金微观结构、致密化行为及硬度的影响。结果表明：掺杂钨精矿石粉末可提高合金组织的细化、均匀化程度，促进其致密性。当钨精矿石粉末与Al-Cu粉末的质量比为3％时，试样的合成密度和硬度最高，分别为3．43g／cm3、HV244．4。
Tungsten/Al- Cu powder compacts with different tungsten powder contents were synthesized by laser combustion. The influences of tungsten powder content on the microstructure, densification and hardness of tungsten/Al- Cu composite were studied by SEM, OM, XRD and Vickers hardness tester. The results show that doped tungsten powders can refine alloys structure, increase the uniformity of alloys and promote densification. When the mass ratio of doped tungsten powder to Al - Cu powder is 3%, the synthesized density and hardness of sample reach the highest values, i.e. 3.43 g/cm3 and HV 244.4.
参考文献
| [1] | 张发云, 闫 洪, 周天瑞, 等. 金属基复合材料制备工艺的研究进展 [J]. 锻压技术, 2006, 36(6): 100-105. |
| [2] | Trojanova Z, Lukac P, Ferkel H, et al. Stability of microsturture in magnesium reinforced by nanoscaled alumina particles [J]. Materials Science and Engineering A, 1997, 234/235/236: 798-801. |
| [3] | 梅 志, 崔 昆, 顾明元, 等. 液态搅拌铸造SiCp及SiO2(P)增强Al-4wt%Mg基复合材料的界面反应研究 [J]. 复合材料学报, 1998, 15(4): 43-47. |
| [4] | 毛 成, 高文理, 苏 海, 等. 搅拌铸造SiCp/A356复合材料的显微组织及力学性能 [J]. 特种铸造及有色合金, 2010, 30(3): 256-258. |
| [5] | 张 鹏, 杜云慧, 曾大本, 等. 铜-石墨复合材料的半固态铸造研究 [J]. 复合材料学报, 2002, 19(1): 42-45. |
| [6] | 秦孝华, 韩维新, 范存淦, 等. 离心铸造法制备陶瓷颗粒增强Al合金基功能梯度复合管 [J]. 金属学报, 2001, 37(10): 1118-1120. |
| [7] | 张永安, 熊柏青, 石力开. 喷射成形技术产品的研究现状 [J]. 材料导报, 2002, 16(3): 11-14. |
| [8] | 李芬芬. 激光烧结多孔金属的成形机理及实验研究 . 南京: 南京航空航天大学, 2008. |
| [9] | 赵昆渝, 朱心昆, 张修庆, 等.自蔓延制备Cu-TiC的研究 [J]. 粉末冶金技术, 2001, 19(4): 222-224. |
| [10] | 赵秦生. 钨精矿铝热还原法生产碳化钨——介绍一种新的碳 化钨生产技术 [J]. 稀有金属与硬质合金, 2003, 31(3): 46-50. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%