为制备室内用可净化空气、低成本的块状活性炭，采用生石油焦为吸附基体原料，沥青为粘结剂，氢氧化钾为活化剂，添加适量陶瓷粉料，经过碾磨混合、成型、隔氧炭化及化学活化制备出块状活性炭试样，对不同试样进行了吸附性能和抗压强度的测试。结果表明：当生石油焦、沥青、氢氧化钾的质量比为10：2：5时，经混合模压成型，在块状活性炭表面涂覆一层泡沫陶瓷浆料，干燥炭化活化后所得块状活性炭试样对甲苯的吸附率为16．7％，抗压强度为3．7MPa，BET比表面积为592．46m2·g-1，总孑乙容为0．2893mL·g-1。
In order to prepare the low-cost blocky activated carbon for indoor air purification, the green petroleum coke was used as the adsorption matrix raw material, the asphalt as the binder and the potassium hydroxide as the activator. The blocky activated carbon samples with proper ceramic powders were prepared after mixing, forming, oxygen isolated carbonization and chemical activation. Adsorption properties and compressive strength tests were conducted on the different samples. The results show that when the mass ratio of petroleum coke,asphalt and potassium hydroxide was 10 2 ： 5 and after compression molding as well as carbon-coated foam ceramic slurry on the prepared sample had a toluene adsorption rate of 16.7% a compressive strength of 3.7 MPa, a BET specific surface area of 592.46 m2· g-1 and a total pore volume of 0. 289 3 mL·g-1
参考文献
| [1] | A. Feaver;G. Cao .Activated carbon cryogels for low pressure methane storage[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(3):590-593. |
| [2] | Xiaoning Wang;Nanwen Zhu;Bingkui Yin .Preparation of sludge-based activated carbon and its application in dye wastewater treatment[J].Journal of hazardous materials,2008(1/2):22-27. |
| [3] | K.Y. Foo .Utilization of biodiesel waste as a renewable resource for activated carbon: Application to environmental problems[J].Renewable & sustainable energy reviews,2009(9):2495-2504. |
| [4] | 李建刚,李开喜,凌立成,贺福,吕春祥.成型活性炭的制备及其甲烷吸附性能的研究[J].新型炭材料,2004(02):114-118. |
| [5] | Andrew K.Kercher;Dennis C.Nagle .Monolithic activated carbon sheets from carbonized medium-density fiberboard[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(1):3-13. |
| [6] | 甘琦,周昕,赵斌元,胡克鳌.成型活性炭的制备研究进展[J].材料导报,2006(01):61-63,68. |
| [7] | 罗道成,刘俊峰.以煤焦油沥青为原料制备高性能活性炭的研究[J].煤化工,2007(03):24-27,35. |
| [8] | Abdel-Nasser A. El-Hendawy .An Insight Into The Koh Activation Mechanism Through The Production Of Microporous Activated Carbon For The Removal Of Pb~(2+) Cations[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(6):3723-3730. |
| [9] | E.A. Dawson;P.A. Barnes;MJ. Chinn .Preparation and characterisiation of carbon-coated ceramic foams for organic vapour adsorption[J].Carbon: An International Journal Sponsored by the American Carbon Society,2006(7):1189-1197. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%