以白云石和工业氧化铝为原料,利用热力学对混合料反应过程进行分析,研究了不同Al2O3含量和烧成温度对CA2-MA复合材料的合成与性能的影响.结果发现:材料经1700℃下煅烧后可获得以CaAl4O7和MgAl2O4为主要物相的复相材料.随着配料中Al2O3含量的增加,材料中CaAl4O7含量减少,CaAl12O19含量增多,且材料显气孔率升高,体积密度略有下降.烧成温度从1600℃提高到1750℃,材料的体积密度增大,显气孔率降低,但温度过高反而有碍烧结,并对高温性能不利.
参考文献
| [1] | Grasset B R;Alzina A.Infuence of thermal damage occurrence at microstructural scale on thethermomechanical behaviour of magnesia-spinel refractories[J].Journal of the European Ceramic Society,2011:1-11. |
| [2] | M.A.L. Braulio;A.G. Tomba Martinez;A.P. Luz .Basic slag attack of spinel-containing refractory castables[J].CERAMICS INTERNATIONAL,2011(6):1935-1945. |
| [3] | D. Mohapatra;D. Sarkar .Preparation of MgO-MgAl_2O_4 composite for refractory application[J].Journal of Materials Processing Technology,2007(1/3):279-283. |
| [4] | 袁林,陈雪峰,陈松林,王杰曾,刘锡俊,曾鲁举,王俊涛.水泥窑用MgO-MgAl2O4-ZrO2-La2O3复合耐火材料的研究[J].水泥,2011(01):4-8. |
| [5] | G.-H. Chen .Mechanical activation of calcium aluminate formation from CaCO_3-Al_2O_3 mixtures[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2006(1/2):279-283. |
| [6] | Jonas S;Nadachawski F .Low thermal expansion refractory composites based on CaAl4O7[J].Ceramics International,1999,25:77-84. |
| [7] | 陈肇友.化学热力学与耐火材料[M].北京:冶金工业出版社,2005:653-654. |
| [8] | 梁英教;车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993:91-228. |
| [9] | 王新锋,阮玉忠,陈永瑞,曾景旭.煅烧温度与保温时间对合成莫来石材料结构与性能的影响[J].硅酸盐通报,2010(04):984-987,991. |
| [10] | 罗旭东,曲殿利,张国栋.二氧化钛对菱镁矿风化石制备铝尖晶石组成结构的影响[J].硅酸盐通报,2011(05):1151-1154. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%